EN 10088-1 X3CrMnNiN20-9-6 vs ASTM A276/A276M S32101

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

EN 10088-1 X3CrMnNiN20-9-6 (EN 10088-1:2023) and ASTM A276/A276M S32101 (ASTM A276/A276M:2017) are both steel grades. Both fall under the Stainless Steel category. EN 10088-1 X3CrMnNiN20-9-6 is defined under European Standard (EN), originating from Europe, while ASTM A276/A276M S32101 is defined under ASTM International, originating from United States.

As per chemical composition, EN 10088-1 X3CrMnNiN20-9-6 vs ASTM A276/A276M S32101 is a 70.1% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With EN 10088-1 X3CrMnNiN20-9-6:
ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
70.1%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property EN 10088-1 X3CrMnNiN20-9-6 ASTM A276/A276M S32101
Standard EN 10088-1:2023 ASTM A276/A276M:2017
Category Stainless Steel Stainless Steel
C (%) <=0.040 <=0.040
Si (%) <=1.00 <=1.00
Mn (%) 8.0-10.0 4.0-6.0
P (%) <=0.045 <=0.040
S (%) <=0.030 <=0.030
Cr (%) 19.0-21.5 21.0-22.0
Mo (%) <=0.75 0.10-0.80
Ni (%) 5.5-7.5 1.35-1.70
N (%) 0.15-0.40 0.20-0.25
Cu (%) Not specified 0.10-0.80
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-1 X3CrMnNiN20-9-6 ASTM A276/A276M S32101
Tensile Strength Not specified >=650 MPa
Yield Strength Not specified >=450 MPa
Elongation Not specified >=30%
Hardness Not specified <=290 HB
Condition Not specified Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed)
Typical Applications
EN 10088-1 X3CrMnNiN20-9-6
Not documented
ASTM A276/A276M S32101
Stainless steel bars and shapes (hot-finished or cold-finished)
Key Differences
Can EN 10088-1 X3CrMnNiN20-9-6 Be Substituted With ASTM A276/A276M S32101?
EN 10088-1 X3CrMnNiN20-9-6 and ASTM A276/A276M S32101 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
EN 10088-1 X3CrMnNiN20-9-6
0 active listings and RFQs →
ASTM A276/A276M S32101
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-1 X3CrMnNiN20-9-6 and ASTM A276/A276M S32101?
ASTM A276/A276M S32101 specifies Cu which is not specified for EN 10088-1 X3CrMnNiN20-9-6.
Can EN 10088-1 X3CrMnNiN20-9-6 be substituted with ASTM A276/A276M S32101?
EN 10088-1 X3CrMnNiN20-9-6 and ASTM A276/A276M S32101 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.