Strong Match — 95.9% match
based on chemical composition and mechanical property overlap.
EN 10088-1 X5CrNi18-10 (EN 10088-1:2023) and IS 6603 X04Cr19Ni9 (IS 6603:2024) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-1 X5CrNi18-10 is defined under European Standard (EN), originating from Europe, while IS 6603 X04Cr19Ni9 is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, EN 10088-1 X5CrNi18-10 vs IS 6603 X04Cr19Ni9 is a 95.9% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a strong match overall at 95.9%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-1 X5CrNi18-10
IS 6603 X04Cr19Ni9
Tensile Strength
Not specified
510-710 MPa
Yield Strength
Not specified
>=200 MPa
Elongation
Not specified
>=40%
Condition
Not specified
Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal)
Typical Applications
EN 10088-1 X5CrNi18-10
Not documented
IS 6603 X04Cr19Ni9
General purposes, semi-finished products, bars, wire rods and bright bars
Can EN 10088-1 X5CrNi18-10 Be Substituted With IS 6603 X04Cr19Ni9?
EN 10088-1 X5CrNi18-10 and IS 6603 X04Cr19Ni9 overlap closely enough on chemistry and mechanical properties that IS 6603 X04Cr19Ni9 is often considered as a substitute for EN 10088-1 X5CrNi18-10 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between EN 10088-1 X5CrNi18-10 and IS 6603 X04Cr19Ni9?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-1 X5CrNi18-10 be substituted with IS 6603 X04Cr19Ni9?
EN 10088-1 X5CrNi18-10 and IS 6603 X04Cr19Ni9 overlap closely enough on chemistry and mechanical properties that IS 6603 X04Cr19Ni9 is often considered as a substitute for EN 10088-1 X5CrNi18-10 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.