EN 10088-1 X5CrNi18-10 vs UNI 6900 X5CrNi1810

Strong Match — 97.2% match based on chemical composition and mechanical property overlap.

EN 10088-1 X5CrNi18-10 (EN 10088-1:2023) and UNI 6900 X5CrNi1810 (UNI 6900:1971) are both steel grades. Both fall under the Stainless Steel category. EN 10088-1 X5CrNi18-10 is defined under European Standard (EN), originating from Europe, while UNI 6900 X5CrNi1810 is defined under Ente Nazionale Italiano di Unificazione (UNI), originating from Italy.

As per chemical composition, EN 10088-1 X5CrNi18-10 vs UNI 6900 X5CrNi1810 is a 97.2% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 97.2%.

Frequently Compared With EN 10088-1 X5CrNi18-10:
GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4845 ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
97.2%
MECHANICAL MATCH
No shared data
OVERALL
97.2%
Specifications
Property EN 10088-1 X5CrNi18-10 UNI 6900 X5CrNi1810
Standard EN 10088-1:2023 UNI 6900:1971
Category Stainless Steel Stainless Steel
C (%) <=0.07 0.07 max
Si (%) <=1.00 1.00 max
Mn (%) <=2.00 2.00 max
P (%) <=0.045 0.045 max
S (%) <=0.015 0.015 max
Cr (%) 17.5-19.5 17.50-19.50
Ni (%) 8.0-10.5 8.00-10.50
N (%) <=0.10 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-1 X5CrNi18-10 UNI 6900 X5CrNi1810
Tensile Strength Not specified 520-720 MPa
Yield Strength Not specified 210 MPa min
Elongation Not specified 45% min
Hardness Not specified 187 HB max
Typical Applications
EN 10088-1 X5CrNi18-10
Not documented
UNI 6900 X5CrNi1810
Used in kitchen equipment, chemical tanks, piping, architectural panels, food processing equipment, and fasteners.
Key Differences
Can EN 10088-1 X5CrNi18-10 Be Substituted With UNI 6900 X5CrNi1810?
EN 10088-1 X5CrNi18-10 and UNI 6900 X5CrNi1810 overlap closely enough on chemistry and mechanical properties that UNI 6900 X5CrNi1810 is often considered as a substitute for EN 10088-1 X5CrNi18-10 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
Forms & Sizes Available on M-EX
EN 10088-1 X5CrNi18-10
No active listings currently.
UNI 6900 X5CrNi1810
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2600–3700 mm (102.36–145.67 in)
On M-EX Right Now
EN 10088-1 X5CrNi18-10
0 active listings and RFQs →
UNI 6900 X5CrNi1810
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-1 X5CrNi18-10 and UNI 6900 X5CrNi1810?
EN 10088-1 X5CrNi18-10 specifies N which is not specified for UNI 6900 X5CrNi1810.
Can EN 10088-1 X5CrNi18-10 be substituted with UNI 6900 X5CrNi1810?
EN 10088-1 X5CrNi18-10 and UNI 6900 X5CrNi1810 overlap closely enough on chemistry and mechanical properties that UNI 6900 X5CrNi1810 is often considered as a substitute for EN 10088-1 X5CrNi18-10 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.