EN 10088-1 X5CrNiCu19-6-2 vs IS 11169 (Part 2) X04Cr18Ni11

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

EN 10088-1 X5CrNiCu19-6-2 (EN 10088-1:2023) and IS 11169 (Part 2) X04Cr18Ni11 (IS 11169 (Part 2):2023) are both steel grades. Both fall under the Stainless Steel category. EN 10088-1 X5CrNiCu19-6-2 is defined under European Standard (EN), originating from Europe, while IS 11169 (Part 2) X04Cr18Ni11 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, EN 10088-1 X5CrNiCu19-6-2 vs IS 11169 (Part 2) X04Cr18Ni11 is a 70.5% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With EN 10088-1 X5CrNiCu19-6-2:
ASTM A959 .- GOST 5632 06Kh23N28 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr13H GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
70.5%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property EN 10088-1 X5CrNiCu19-6-2 IS 11169 (Part 2) X04Cr18Ni11
Standard EN 10088-1:2023 IS 11169 (Part 2):2023
Category Stainless Steel Stainless Steel
C (%) 0.030-0.08 <=0.08
Si (%) <=0.50 <=1.00
Mn (%) 1.50-4.0 <=2.00
P (%) <=0.045 <=0.045
S (%) <=0.015 <=0.030
Cr (%) 18.0-19.0 17.0-19.0
Ni (%) 5.5-6.9 10.5-13.0
N (%) 0.030-0.11 <=0.10
Cu (%) 1.30-2.00 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-1 X5CrNiCu19-6-2 IS 11169 (Part 2) X04Cr18Ni11
Reduction of Area, solution annealed (+AT) Not specified >=65% (over 5 to 50 mm)
Tensile Strength, solution annealed (+AT) Not specified <=650 MPa (over 5 to 50 mm)
Typical Applications
EN 10088-1 X5CrNiCu19-6-2
Not documented
IS 11169 (Part 2) X04Cr18Ni11
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, Table 11)
Key Differences
Can EN 10088-1 X5CrNiCu19-6-2 Be Substituted With IS 11169 (Part 2) X04Cr18Ni11?
EN 10088-1 X5CrNiCu19-6-2 and IS 11169 (Part 2) X04Cr18Ni11 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
EN 10088-1 X5CrNiCu19-6-2
0 active listings and RFQs →
IS 11169 (Part 2) X04Cr18Ni11
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-1 X5CrNiCu19-6-2 and IS 11169 (Part 2) X04Cr18Ni11?
EN 10088-1 X5CrNiCu19-6-2 specifies Cu which is not specified for IS 11169 (Part 2) X04Cr18Ni11.
Can EN 10088-1 X5CrNiCu19-6-2 be substituted with IS 11169 (Part 2) X04Cr18Ni11?
EN 10088-1 X5CrNiCu19-6-2 and IS 11169 (Part 2) X04Cr18Ni11 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.