EN 10088-1 X5CrNiCu19-6-2 vs IS 11169 (Part 2) X04Cr18Ni9Cu
Related Material — 69.9% match
based on chemical composition and mechanical property overlap.
EN 10088-1 X5CrNiCu19-6-2 (EN 10088-1:2023) and IS 11169 (Part 2) X04Cr18Ni9Cu (IS 11169 (Part 2):2023) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-1 X5CrNiCu19-6-2 is defined under European Standard (EN), originating from Europe, while IS 11169 (Part 2) X04Cr18Ni9Cu is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, EN 10088-1 X5CrNiCu19-6-2 vs IS 11169 (Part 2) X04Cr18Ni9Cu is a 71.5% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a related material overall at 69.9%.
Frequently Compared With EN 10088-1 X5CrNiCu19-6-2:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-1 X5CrNiCu19-6-2
IS 11169 (Part 2) X04Cr18Ni9Cu
Reduction of Area, cold drawn and solution annealed (+AT+C+AT)
Not specified
>=60% (0.8 to 5 mm) / >=65% (over 5 to 25 mm)
Tensile Strength, cold drawn and solution annealed (+AT+C+AT)
Not specified
<=710 MPa (0.8 to 2 mm) / <=700 MPa (over 2 to 5 mm) / <=650 MPa (over 5 to 25 mm)
Typical Applications
EN 10088-1 X5CrNiCu19-6-2
Not documented
IS 11169 (Part 2) X04Cr18Ni9Cu
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, Table 11)
Can EN 10088-1 X5CrNiCu19-6-2 Be Substituted With IS 11169 (Part 2) X04Cr18Ni9Cu?
EN 10088-1 X5CrNiCu19-6-2 and IS 11169 (Part 2) X04Cr18Ni9Cu share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between EN 10088-1 X5CrNiCu19-6-2 and IS 11169 (Part 2) X04Cr18Ni9Cu?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-1 X5CrNiCu19-6-2 be substituted with IS 11169 (Part 2) X04Cr18Ni9Cu?
EN 10088-1 X5CrNiCu19-6-2 and IS 11169 (Part 2) X04Cr18Ni9Cu share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.