EN 10088-1 X6CrMnNiN18-13-3 vs ASTM A240/A240M S24000
Strong Match — 98.6% match
based on chemical composition and mechanical property overlap.
EN 10088-1 X6CrMnNiN18-13-3 (EN 10088-1:2023) and ASTM A240/A240M S24000 (ASTM A240/A240M:2025) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-1 X6CrMnNiN18-13-3 is defined under European Standard (EN), originating from Europe, while ASTM A240/A240M S24000 is defined under ASTM International, originating from United States.
As per chemical composition, EN 10088-1 X6CrMnNiN18-13-3 vs ASTM A240/A240M S24000 is a 98.6% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a strong match overall at 98.6%.
Frequently Compared With EN 10088-1 X6CrMnNiN18-13-3:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-1 X6CrMnNiN18-13-3
ASTM A240/A240M S24000
Tensile Strength
Not specified
>=690 MPa
Yield Strength
Not specified
>=415 MPa
Elongation
Not specified
>=40%
Hardness
Not specified
<=241 HB
Condition
Not specified
Sheet and strip (first condition printed); yield by 0.2 percent offset
Typical Applications
EN 10088-1 X6CrMnNiN18-13-3
Not documented
ASTM A240/A240M S24000
Pressure vessels and general applications (plate, sheet and strip)
Can EN 10088-1 X6CrMnNiN18-13-3 Be Substituted With ASTM A240/A240M S24000?
EN 10088-1 X6CrMnNiN18-13-3 and ASTM A240/A240M S24000 overlap closely enough on chemistry and mechanical properties that ASTM A240/A240M S24000 is often considered as a substitute for EN 10088-1 X6CrMnNiN18-13-3 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between EN 10088-1 X6CrMnNiN18-13-3 and ASTM A240/A240M S24000?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-1 X6CrMnNiN18-13-3 be substituted with ASTM A240/A240M S24000?
EN 10088-1 X6CrMnNiN18-13-3 and ASTM A240/A240M S24000 overlap closely enough on chemistry and mechanical properties that ASTM A240/A240M S24000 is often considered as a substitute for EN 10088-1 X6CrMnNiN18-13-3 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.