EN 10088-1 X6CrMoNb17-1 vs IS 11169 (Part 2) X04Cr17Mo1
Strong Match — 96.9% match
based on chemical composition and mechanical property overlap.
EN 10088-1 X6CrMoNb17-1 (EN 10088-1:2023) and IS 11169 (Part 2) X04Cr17Mo1 (IS 11169 (Part 2):2023) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-1 X6CrMoNb17-1 is defined under European Standard (EN), originating from Europe, while IS 11169 (Part 2) X04Cr17Mo1 is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, EN 10088-1 X6CrMoNb17-1 vs IS 11169 (Part 2) X04Cr17Mo1 is a 96.9% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a strong match overall at 96.9%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-1 X6CrMoNb17-1
IS 11169 (Part 2) X04Cr17Mo1
Reduction of Area, soft annealed (+A)
Not specified
>=60% (over 5 to 25 mm)
Tensile Strength, soft annealed (+A)
Not specified
<=600 MPa (over 5 to 25 mm)
Typical Applications
EN 10088-1 X6CrMoNb17-1
Not documented
IS 11169 (Part 2) X04Cr17Mo1
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 25 mm (clause 1.1, Table 13)
Key Differences
EN 10088-1 X6CrMoNb17-1 specifies N which is not specified for IS 11169 (Part 2) X04Cr17Mo1.
Can EN 10088-1 X6CrMoNb17-1 Be Substituted With IS 11169 (Part 2) X04Cr17Mo1?
EN 10088-1 X6CrMoNb17-1 and IS 11169 (Part 2) X04Cr17Mo1 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 2) X04Cr17Mo1 is often considered as a substitute for EN 10088-1 X6CrMoNb17-1 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between EN 10088-1 X6CrMoNb17-1 and IS 11169 (Part 2) X04Cr17Mo1?
EN 10088-1 X6CrMoNb17-1 specifies N which is not specified for IS 11169 (Part 2) X04Cr17Mo1.
Can EN 10088-1 X6CrMoNb17-1 be substituted with IS 11169 (Part 2) X04Cr17Mo1?
EN 10088-1 X6CrMoNb17-1 and IS 11169 (Part 2) X04Cr17Mo1 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 2) X04Cr17Mo1 is often considered as a substitute for EN 10088-1 X6CrMoNb17-1 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.