EN 10088-1 X6CrMoS17 vs IS 11169 (Part 2) X04Cr17Mo1
Close Alternative — 84.9% match
based on chemical composition and mechanical property overlap.
EN 10088-1 X6CrMoS17 (EN 10088-1:2023) and IS 11169 (Part 2) X04Cr17Mo1 (IS 11169 (Part 2):2023) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-1 X6CrMoS17 is defined under European Standard (EN), originating from Europe, while IS 11169 (Part 2) X04Cr17Mo1 is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, EN 10088-1 X6CrMoS17 vs IS 11169 (Part 2) X04Cr17Mo1 is a 85.2% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a close alternative overall at 84.9%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-1 X6CrMoS17
IS 11169 (Part 2) X04Cr17Mo1
Reduction of Area, soft annealed (+A)
Not specified
>=60% (over 5 to 25 mm)
Tensile Strength, soft annealed (+A)
Not specified
<=600 MPa (over 5 to 25 mm)
Typical Applications
EN 10088-1 X6CrMoS17
Not documented
IS 11169 (Part 2) X04Cr17Mo1
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 25 mm (clause 1.1, Table 13)
Can EN 10088-1 X6CrMoS17 Be Substituted With IS 11169 (Part 2) X04Cr17Mo1?
EN 10088-1 X6CrMoS17 and IS 11169 (Part 2) X04Cr17Mo1 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
What is the difference between EN 10088-1 X6CrMoS17 and IS 11169 (Part 2) X04Cr17Mo1?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-1 X6CrMoS17 be substituted with IS 11169 (Part 2) X04Cr17Mo1?
EN 10088-1 X6CrMoS17 and IS 11169 (Part 2) X04Cr17Mo1 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.