Strong Match — 85.5% match
based on chemical composition and mechanical property overlap.
EN 10088-1 X6CrNi18-10 (EN 10088-1:2023) and GB/T 3280 06Cr19Ni10 (GB/T 3280-2015) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-1 X6CrNi18-10 is defined under European Standard (EN), originating from Europe, while GB/T 3280 06Cr19Ni10 is defined under Guobiao Standards (GB/T), originating from China.
As per chemical composition, EN 10088-1 X6CrNi18-10 vs GB/T 3280 06Cr19Ni10 is a 85.5% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a strong match overall at 85.5%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-1 X6CrNi18-10
GB/T 3280 06Cr19Ni10
Tensile Strength
Not specified
520-720 MPa
Yield Strength
Not specified
205-310 MPa
Elongation
Not specified
40-60%
Hardness
Not specified
187 HB max
Typical Applications
EN 10088-1 X6CrNi18-10
Not documented
GB/T 3280 06Cr19Ni10
Used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners.
Key Differences
EN 10088-1 X6CrNi18-10 specifies N which is not specified for GB/T 3280 06Cr19Ni10.
Can EN 10088-1 X6CrNi18-10 Be Substituted With GB/T 3280 06Cr19Ni10?
EN 10088-1 X6CrNi18-10 and GB/T 3280 06Cr19Ni10 overlap closely enough on chemistry and mechanical properties that GB/T 3280 06Cr19Ni10 is often considered as a substitute for EN 10088-1 X6CrNi18-10 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between EN 10088-1 X6CrNi18-10 and GB/T 3280 06Cr19Ni10?
EN 10088-1 X6CrNi18-10 specifies N which is not specified for GB/T 3280 06Cr19Ni10.
Can EN 10088-1 X6CrNi18-10 be substituted with GB/T 3280 06Cr19Ni10?
EN 10088-1 X6CrNi18-10 and GB/T 3280 06Cr19Ni10 overlap closely enough on chemistry and mechanical properties that GB/T 3280 06Cr19Ni10 is often considered as a substitute for EN 10088-1 X6CrNi18-10 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.