EN 10088-1 X6NiCrSiNCe35-25 vs IS 6911 X20Cr25Ni20
Related Material — 69.9% match
based on chemical composition and mechanical property overlap.
EN 10088-1 X6NiCrSiNCe35-25 (EN 10088-1:2023) and IS 6911 X20Cr25Ni20 (IS 6911:1992) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-1 X6NiCrSiNCe35-25 is defined under European Standard (EN), originating from Europe, while IS 6911 X20Cr25Ni20 is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, EN 10088-1 X6NiCrSiNCe35-25 vs IS 6911 X20Cr25Ni20 is a 73.6% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a related material overall at 69.9%.
Frequently Compared With EN 10088-1 X6NiCrSiNCe35-25:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-1 X6NiCrSiNCe35-25
IS 6911 X20Cr25Ni20
Bend Test (180 deg)
Not specified
Not required
Elongation (50 mm, annealed)
Not specified
>=40%
Hardness (annealed, max)
Not specified
217 HBS, 95 HRB
Tensile Strength (annealed)
Not specified
>=490 MPa
Yield Strength (0.2% proof, annealed)
Not specified
>=210 MPa
Typical Applications
EN 10088-1 X6NiCrSiNCe35-25
Not documented
IS 6911 X20Cr25Ni20
Stainless and heat-resisting steel plate, sheet and strip (clause 1.1)
Key Differences
EN 10088-1 X6NiCrSiNCe35-25 specifies N, Ce which are not specified for IS 6911 X20Cr25Ni20.
Can EN 10088-1 X6NiCrSiNCe35-25 Be Substituted With IS 6911 X20Cr25Ni20?
EN 10088-1 X6NiCrSiNCe35-25 and IS 6911 X20Cr25Ni20 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between EN 10088-1 X6NiCrSiNCe35-25 and IS 6911 X20Cr25Ni20?
EN 10088-1 X6NiCrSiNCe35-25 specifies N, Ce which are not specified for IS 6911 X20Cr25Ni20.
Can EN 10088-1 X6NiCrSiNCe35-25 be substituted with IS 6911 X20Cr25Ni20?
EN 10088-1 X6NiCrSiNCe35-25 and IS 6911 X20Cr25Ni20 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.