EN 10088-1 X5CrNi18-10 vs EN 10088-1 1.4006

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

EN 10088-1 X5CrNi18-10 (EN 10088-1:2014) and EN 10088-1 1.4006 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. EN 10088-1 X5CrNi18-10 is typically used for food, chemical, architectural applications, while EN 10088-1 1.4006 is commonly used for cutlery, turbine blades, fasteners, surgical instruments. EN 10088-1 X5CrNi18-10 is defined under European Standard (EN), originating from Europe, while EN 10088-1 1.4006 is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10088-1 X5CrNi18-10 vs EN 10088-1 1.4006 is a 59.3% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With EN 10088-1 X5CrNi18-10:
GOST 5632 08X18H10 EN 10088-1 1.4301 GOST 5632 06Kh23N28 EN 10088-1 1.4845 GOST 5632 12Kh13 EN 10088-1 1.4401 GB/T 3280 06Cr19Ni10 ASTM A959 .- IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 11Cr17Ni13W3TiH
Match Breakdown
CHEMISTRY MATCH
59.3%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property EN 10088-1 X5CrNi18-10 EN 10088-1 1.4006
Standard EN 10088-1:2014 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.07 0.08–0.15
Si (%) <=1.00 ≤1.00
Mn (%) <=2.00 ≤1.50
P (%) <=0.045 Not specified
S (%) <=0.015 Not specified
Cr (%) 17.5-19.5 11.5–13.5
Ni (%) 8.0-10.5 ≤0.75
N (%) <=0.10 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-1 X5CrNi18-10 EN 10088-1 1.4006
Tensile Strength Not specified ≥540 MPa (annealed)
Hardness HRC Not specified 36–45 (hardened)
Elongation Not specified ≥18%
Typical Applications
EN 10088-1 X5CrNi18-10
Food, chemical, architectural applications
EN 10088-1 1.4006
Cutlery, turbine blades, fasteners, surgical instruments
Key Differences
Can EN 10088-1 X5CrNi18-10 Be Substituted With EN 10088-1 1.4006?
EN 10088-1 X5CrNi18-10 and EN 10088-1 1.4006 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
EN 10088-1 X5CrNi18-10
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2500–3900 mm (98.43–153.54 in)
EN 10088-1 1.4006
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2700–3400 mm (106.3–133.86 in)
On M-EX Right Now
EN 10088-1 X5CrNi18-10
3 active listings and RFQs →
EN 10088-1 1.4006
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-1 X5CrNi18-10 and EN 10088-1 1.4006?
EN 10088-1 X5CrNi18-10 specifies P, S, N which are not specified for EN 10088-1 1.4006.
Can EN 10088-1 X5CrNi18-10 be substituted with EN 10088-1 1.4006?
EN 10088-1 X5CrNi18-10 and EN 10088-1 1.4006 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.