EN 10088-2 X10CrNi18-8 vs EN 10088-1 X6CrNiCuS18-9-2

Close Alternative — 74.9% match based on chemical composition and mechanical property overlap.

EN 10088-2 X10CrNi18-8 (EN 10088-2:2014) and EN 10088-1 X6CrNiCuS18-9-2 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. EN 10088-2 X10CrNi18-8 is defined under European Standard (EN), originating from Europe, while EN 10088-1 X6CrNiCuS18-9-2 is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10088-2 X10CrNi18-8 vs EN 10088-1 X6CrNiCuS18-9-2 is a 74.9% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 74.9%.

Frequently Compared With EN 10088-2 X10CrNi18-8:
ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo EN 10088-1 1.4006 IS 1570 (Part 7) 11Cr17Ni13W3TiH
Match Breakdown
CHEMISTRY MATCH
74.9%
MECHANICAL MATCH
No shared data
OVERALL
74.9%
Specifications
Property EN 10088-2 X10CrNi18-8 EN 10088-1 X6CrNiCuS18-9-2
Standard EN 10088-2:2014 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) 0.05-0.15 <=0.08
Si (%) <=2.00 <=1.00
Mn (%) <=2.00 <=2.00
P (%) <=0.045 <=0.045
S (%) <=0.015 0.15-0.35
Cr (%) 16.0-19.0 17.0-19.0
Mo (%) <=0.80 <=0.60
Ni (%) 6.0-9.5 8.0-10.0
N (%) <=0.10 <=0.10
Cu (%) Not specified 1.40-1.80
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-2 X10CrNi18-8 EN 10088-1 X6CrNiCuS18-9-2
Tensile Strength 600-950 MPa Not specified
Yield Strength >=250 MPa Not specified
Elongation >=40% Not specified
Condition Solution annealed (+AT), cold rolled strip, up to 8 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick Not specified
Typical Applications
EN 10088-2 X10CrNi18-8
General purposes, hot or cold rolled sheet/plate and strip
EN 10088-1 X6CrNiCuS18-9-2
Not documented
Key Differences
Can EN 10088-2 X10CrNi18-8 Be Substituted With EN 10088-1 X6CrNiCuS18-9-2?
EN 10088-2 X10CrNi18-8 and EN 10088-1 X6CrNiCuS18-9-2 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
EN 10088-2 X10CrNi18-8
0 active listings and RFQs →
EN 10088-1 X6CrNiCuS18-9-2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-2 X10CrNi18-8 and EN 10088-1 X6CrNiCuS18-9-2?
EN 10088-1 X6CrNiCuS18-9-2 specifies Cu which is not specified for EN 10088-2 X10CrNi18-8.
Can EN 10088-2 X10CrNi18-8 be substituted with EN 10088-1 X6CrNiCuS18-9-2?
EN 10088-2 X10CrNi18-8 and EN 10088-1 X6CrNiCuS18-9-2 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.