EN 10088-2 X11CrNiMnN19-8-6 vs IS 6603 X11Cr19Ni8Mn6N
Strong Match — 100% match
based on chemical composition and mechanical property overlap.
EN 10088-2 X11CrNiMnN19-8-6 (EN 10088-2:2014) and IS 6603 X11Cr19Ni8Mn6N (IS 6603:2024) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-2 X11CrNiMnN19-8-6 is typically used for general purposes, hot or cold rolled sheet/plate and strip, while IS 6603 X11Cr19Ni8Mn6N is commonly used for general purposes, semi-finished products, bars, wire rods and bright bars.
EN 10088-2 X11CrNiMnN19-8-6 is defined under European Standard (EN), originating from Europe, while IS 6603 X11Cr19Ni8Mn6N is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, EN 10088-2 X11CrNiMnN19-8-6 vs IS 6603 X11Cr19Ni8Mn6N is a 100% match.
As per mechanical properties, the match is 100%.
Combined, this makes them a strong match overall at 100%.
Frequently Compared With EN 10088-2 X11CrNiMnN19-8-6:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-2 X11CrNiMnN19-8-6
IS 6603 X11Cr19Ni8Mn6N
Tensile Strength
750-950 MPa
750-950 MPa
Yield Strength
>=340 MPa
>=340 MPa
Elongation
>=35%
Not specified
Condition
Solution annealed (+AT), cold rolled strip, up to 4 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick
Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 15 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal)
Typical Applications
EN 10088-2 X11CrNiMnN19-8-6
General purposes, hot or cold rolled sheet/plate and strip
IS 6603 X11Cr19Ni8Mn6N
General purposes, semi-finished products, bars, wire rods and bright bars
Can EN 10088-2 X11CrNiMnN19-8-6 Be Substituted With IS 6603 X11Cr19Ni8Mn6N?
EN 10088-2 X11CrNiMnN19-8-6 and IS 6603 X11Cr19Ni8Mn6N overlap closely enough on chemistry and mechanical properties that IS 6603 X11Cr19Ni8Mn6N is often considered as a substitute for EN 10088-2 X11CrNiMnN19-8-6 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between EN 10088-2 X11CrNiMnN19-8-6 and IS 6603 X11Cr19Ni8Mn6N?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-2 X11CrNiMnN19-8-6 be substituted with IS 6603 X11Cr19Ni8Mn6N?
EN 10088-2 X11CrNiMnN19-8-6 and IS 6603 X11Cr19Ni8Mn6N overlap closely enough on chemistry and mechanical properties that IS 6603 X11Cr19Ni8Mn6N is often considered as a substitute for EN 10088-2 X11CrNiMnN19-8-6 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.