EN 10088-2 X12CrMnNiN17-7-5 vs EN 10088-1 X8CrMnNi19-6-3

Close Alternative — 81.1% match based on chemical composition and mechanical property overlap.

EN 10088-2 X12CrMnNiN17-7-5 (EN 10088-2:2014) and EN 10088-1 X8CrMnNi19-6-3 (EN 10088-1:2023) are both steel grades. Both fall under the Stainless Steel category. EN 10088-2 X12CrMnNiN17-7-5 is defined under European Standard (EN), originating from Europe, while EN 10088-1 X8CrMnNi19-6-3 is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10088-2 X12CrMnNiN17-7-5 vs EN 10088-1 X8CrMnNi19-6-3 is a 81.1% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 81.1%.

Frequently Compared With EN 10088-2 X12CrMnNiN17-7-5:
ASTM A959 201 ASTM A959 202 ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH
Match Breakdown
CHEMISTRY MATCH
81.1%
MECHANICAL MATCH
No shared data
OVERALL
81.1%
Specifications
Property EN 10088-2 X12CrMnNiN17-7-5 EN 10088-1 X8CrMnNi19-6-3
Standard EN 10088-2:2014 EN 10088-1:2023
Category Stainless Steel Stainless Steel
C (%) <=0.15 <=0.10
Si (%) <=1.00 <=1.00
Mn (%) 5.5-7.5 5.0-8.0
P (%) <=0.045 <=0.045
S (%) <=0.015 <=0.015
Cr (%) 16.0-18.0 17.0-20.5
Ni (%) 3.5-5.5 2.00-4.5
N (%) 0.05-0.25 <=0.30
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-2 X12CrMnNiN17-7-5 EN 10088-1 X8CrMnNi19-6-3
Tensile Strength 680-880 MPa Not specified
Yield Strength >=350 MPa Not specified
Elongation >=45% Not specified
Condition Solution annealed (+AT), cold rolled strip, up to 8 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick Not specified
Typical Applications
EN 10088-2 X12CrMnNiN17-7-5
General purposes, hot or cold rolled sheet/plate and strip
EN 10088-1 X8CrMnNi19-6-3
Not documented
Can EN 10088-2 X12CrMnNiN17-7-5 Be Substituted With EN 10088-1 X8CrMnNi19-6-3?
EN 10088-2 X12CrMnNiN17-7-5 and EN 10088-1 X8CrMnNi19-6-3 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
EN 10088-2 X12CrMnNiN17-7-5
0 active listings and RFQs →
EN 10088-1 X8CrMnNi19-6-3
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-2 X12CrMnNiN17-7-5 and EN 10088-1 X8CrMnNi19-6-3?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-2 X12CrMnNiN17-7-5 be substituted with EN 10088-1 X8CrMnNi19-6-3?
EN 10088-2 X12CrMnNiN17-7-5 and EN 10088-1 X8CrMnNi19-6-3 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.