EN 10088-2 X1CrNi25-21 vs EN 10088-1 X1CrNiMoN25-22-2
Related Material — 69.9% match
based on chemical composition and mechanical property overlap.
EN 10088-2 X1CrNi25-21 (EN 10088-2:2014) and EN 10088-1 X1CrNiMoN25-22-2 (EN 10088-1:2014) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-2 X1CrNi25-21 is defined under European Standard (EN), originating from Europe, while EN 10088-1 X1CrNiMoN25-22-2 is defined under European Standard (EN), originating from Europe.
As per chemical composition, EN 10088-2 X1CrNi25-21 vs EN 10088-1 X1CrNiMoN25-22-2 is a 77% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a related material overall at 69.9%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-2 X1CrNi25-21
EN 10088-1 X1CrNiMoN25-22-2
Tensile Strength
470-670 MPa
Not specified
Yield Strength
>=200 MPa
Not specified
Elongation
>=40%
Not specified
Condition
Solution annealed (+AT), hot rolled plate, up to 75 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick
Not specified
Typical Applications
EN 10088-2 X1CrNi25-21
General purposes, hot or cold rolled sheet/plate and strip
EN 10088-1 X1CrNiMoN25-22-2
Not documented
Can EN 10088-2 X1CrNi25-21 Be Substituted With EN 10088-1 X1CrNiMoN25-22-2?
EN 10088-2 X1CrNi25-21 and EN 10088-1 X1CrNiMoN25-22-2 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between EN 10088-2 X1CrNi25-21 and EN 10088-1 X1CrNiMoN25-22-2?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-2 X1CrNi25-21 be substituted with EN 10088-1 X1CrNiMoN25-22-2?
EN 10088-2 X1CrNi25-21 and EN 10088-1 X1CrNiMoN25-22-2 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.