EN 10088-2 X1CrNiMoCuN24-22-8 vs EN 10088-1 X1CrNiMoCuN24-22-8

Strong Match — 100% match based on chemical composition and mechanical property overlap.

EN 10088-2 X1CrNiMoCuN24-22-8 (EN 10088-2:2014) and EN 10088-1 X1CrNiMoCuN24-22-8 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. EN 10088-2 X1CrNiMoCuN24-22-8 is defined under European Standard (EN), originating from Europe, while EN 10088-1 X1CrNiMoCuN24-22-8 is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10088-2 X1CrNiMoCuN24-22-8 vs EN 10088-1 X1CrNiMoCuN24-22-8 is a 100% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 100%.

Frequently Compared With EN 10088-2 X1CrNiMoCuN24-22-8:
GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
100%
MECHANICAL MATCH
No shared data
OVERALL
100%
Specifications
Property EN 10088-2 X1CrNiMoCuN24-22-8 EN 10088-1 X1CrNiMoCuN24-22-8
Standard EN 10088-2:2014 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.020 <=0.020
Si (%) <=0.50 <=0.50
Mn (%) 2.00-4.0 2.00-4.0
P (%) <=0.030 <=0.030
S (%) <=0.005 <=0.005
Cr (%) 23.0-25.0 23.0-25.0
Mo (%) 7.0-8.0 7.0-8.0
Ni (%) 21.0-23.0 21.0-23.0
N (%) 0.45-0.55 0.45-0.55
Cu (%) 0.30-0.60 0.30-0.60
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-2 X1CrNiMoCuN24-22-8 EN 10088-1 X1CrNiMoCuN24-22-8
Tensile Strength 750-1000 MPa Not specified
Yield Strength >=430 MPa Not specified
Elongation >=40% Not specified
Condition Solution annealed (+AT), cold rolled strip, up to 8 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick Not specified
Typical Applications
EN 10088-2 X1CrNiMoCuN24-22-8
General purposes, hot or cold rolled sheet/plate and strip
EN 10088-1 X1CrNiMoCuN24-22-8
Not documented
Can EN 10088-2 X1CrNiMoCuN24-22-8 Be Substituted With EN 10088-1 X1CrNiMoCuN24-22-8?
EN 10088-2 X1CrNiMoCuN24-22-8 and EN 10088-1 X1CrNiMoCuN24-22-8 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X1CrNiMoCuN24-22-8 is often considered as a substitute for EN 10088-2 X1CrNiMoCuN24-22-8 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
EN 10088-2 X1CrNiMoCuN24-22-8
0 active listings and RFQs →
EN 10088-1 X1CrNiMoCuN24-22-8
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-2 X1CrNiMoCuN24-22-8 and EN 10088-1 X1CrNiMoCuN24-22-8?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-2 X1CrNiMoCuN24-22-8 be substituted with EN 10088-1 X1CrNiMoCuN24-22-8?
EN 10088-2 X1CrNiMoCuN24-22-8 and EN 10088-1 X1CrNiMoCuN24-22-8 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X1CrNiMoCuN24-22-8 is often considered as a substitute for EN 10088-2 X1CrNiMoCuN24-22-8 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.