EN 10088-2 X1CrNiMoCuN25-25-5 vs ASTM A959 N08926

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

EN 10088-2 X1CrNiMoCuN25-25-5 (EN 10088-2:2014) and ASTM A959 N08926 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. EN 10088-2 X1CrNiMoCuN25-25-5 is typically used for general purposes, hot or cold rolled sheet/plate and strip, while ASTM A959 N08926 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). EN 10088-2 X1CrNiMoCuN25-25-5 is defined under European Standard (EN), originating from Europe, while ASTM A959 N08926 is defined under ASTM International, originating from United States.

As per chemical composition, EN 10088-2 X1CrNiMoCuN25-25-5 vs ASTM A959 N08926 is a 76% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With EN 10088-2 X1CrNiMoCuN25-25-5:
GOST 5632 06Kh23N28 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12Ni2Mo GB/T 3280 06Cr19Ni10 EN 10088-1 1.4006 IS 1570 (Part 7) 11Cr17Ni13W3TiH ASTM A959 .- GOST 5632 08X18H10 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
76%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property EN 10088-2 X1CrNiMoCuN25-25-5 ASTM A959 N08926
Standard EN 10088-2:2014 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.020 <=0.020
Si (%) <=0.70 <=0.50
Mn (%) <=2.00 <=2.00
P (%) <=0.030 <=0.030
S (%) <=0.010 <=0.010
Cr (%) 24.0-26.0 19.0-21.0
Mo (%) 4.7-5.7 6.0-7.0
Ni (%) 24.0-27.0 24.0-26.0
N (%) 0.17-0.25 0.15-0.25
Cu (%) 1.00-2.00 0.50-1.50
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-2 X1CrNiMoCuN25-25-5 ASTM A959 N08926
Tensile Strength 600-800 MPa Not specified
Yield Strength >=290 MPa Not specified
Elongation >=40% Not specified
Condition Solution annealed (+AT), hot rolled plate, up to 75 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick Not specified
Typical Applications
EN 10088-2 X1CrNiMoCuN25-25-5
General purposes, hot or cold rolled sheet/plate and strip
ASTM A959 N08926
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Can EN 10088-2 X1CrNiMoCuN25-25-5 Be Substituted With ASTM A959 N08926?
EN 10088-2 X1CrNiMoCuN25-25-5 and ASTM A959 N08926 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
EN 10088-2 X1CrNiMoCuN25-25-5
0 active listings and RFQs →
ASTM A959 N08926
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-2 X1CrNiMoCuN25-25-5 and ASTM A959 N08926?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-2 X1CrNiMoCuN25-25-5 be substituted with ASTM A959 N08926?
EN 10088-2 X1CrNiMoCuN25-25-5 and ASTM A959 N08926 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.