Related Material — 69.9% match
based on chemical composition and mechanical property overlap.
EN 10088-2 X1CrNiMoCuN25-25-5 (EN 10088-2:2014) and ASTM A959 S32520 (ASTM A959:2011) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-2 X1CrNiMoCuN25-25-5 is typically used for general purposes, hot or cold rolled sheet/plate and strip, while ASTM A959 S32520 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1).
EN 10088-2 X1CrNiMoCuN25-25-5 is defined under European Standard (EN), originating from Europe, while ASTM A959 S32520 is defined under ASTM International, originating from United States.
As per chemical composition, EN 10088-2 X1CrNiMoCuN25-25-5 vs ASTM A959 S32520 is a 71.9% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a related material overall at 69.9%.
Frequently Compared With EN 10088-2 X1CrNiMoCuN25-25-5:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-2 X1CrNiMoCuN25-25-5
ASTM A959 S32520
Tensile Strength
600-800 MPa
Not specified
Yield Strength
>=290 MPa
Not specified
Elongation
>=40%
Not specified
Condition
Solution annealed (+AT), hot rolled plate, up to 75 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick
Not specified
Typical Applications
EN 10088-2 X1CrNiMoCuN25-25-5
General purposes, hot or cold rolled sheet/plate and strip
ASTM A959 S32520
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Can EN 10088-2 X1CrNiMoCuN25-25-5 Be Substituted With ASTM A959 S32520?
EN 10088-2 X1CrNiMoCuN25-25-5 and ASTM A959 S32520 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between EN 10088-2 X1CrNiMoCuN25-25-5 and ASTM A959 S32520?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-2 X1CrNiMoCuN25-25-5 be substituted with ASTM A959 S32520?
EN 10088-2 X1CrNiMoCuN25-25-5 and ASTM A959 S32520 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.