EN 10088-2 X1CrNiMoCuN25-25-5 vs EN 10088-3 X1CrNiMoCuN25-25-5

Close Alternative — 77.8% match based on chemical composition and mechanical property overlap.

EN 10088-2 X1CrNiMoCuN25-25-5 (EN 10088-2:2014) and EN 10088-3 X1CrNiMoCuN25-25-5 (EN 10088-3:2014) are both steel grades. Both fall under the Stainless Steel category. EN 10088-2 X1CrNiMoCuN25-25-5 is typically used for general purposes, hot or cold rolled sheet/plate and strip, while EN 10088-3 X1CrNiMoCuN25-25-5 is commonly used for general purposes, semi-finished products, bars, rods, wire, sections and bright products. EN 10088-2 X1CrNiMoCuN25-25-5 is defined under European Standard (EN), originating from Europe, while EN 10088-3 X1CrNiMoCuN25-25-5 is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10088-2 X1CrNiMoCuN25-25-5 vs EN 10088-3 X1CrNiMoCuN25-25-5 is a 100% match. As per mechanical properties, the match is 33.3%. Combined, this makes them a close alternative overall at 77.8%.

Frequently Compared With EN 10088-2 X1CrNiMoCuN25-25-5:
GOST 5632 06Kh23N28 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12Ni2Mo GB/T 3280 06Cr19Ni10 EN 10088-1 1.4006 IS 1570 (Part 7) 11Cr17Ni13W3TiH ASTM A959 .- GOST 5632 08X18H10 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
100%
MECHANICAL MATCH
33.3%
OVERALL
77.8%
Specifications
Property EN 10088-2 X1CrNiMoCuN25-25-5 EN 10088-3 X1CrNiMoCuN25-25-5
Standard EN 10088-2:2014 EN 10088-3:2014
Category Stainless Steel Stainless Steel
C (%) <=0.020 <=0.020
Si (%) <=0.70 <=0.70
Mn (%) <=2.00 <=2.00
P (%) <=0.030 <=0.030
S (%) <=0.010 <=0.010
Cr (%) 24.0-26.0 24.0-26.0
Mo (%) 4.7-5.7 4.7-5.7
Ni (%) 24.0-27.0 24.0-27.0
N (%) 0.17-0.25 0.17-0.25
Cu (%) 1.00-2.00 1.00-2.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-2 X1CrNiMoCuN25-25-5 EN 10088-3 X1CrNiMoCuN25-25-5
Tensile Strength 600-800 MPa 600-800 MPa
Yield Strength >=290 MPa >=300 MPa
Elongation >=40% >=35%
Condition Solution annealed (+AT), hot rolled plate, up to 75 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick Solution annealed (+AT), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal), hardness for guidance only
Hardness Not specified <=250 HB
Typical Applications
EN 10088-2 X1CrNiMoCuN25-25-5
General purposes, hot or cold rolled sheet/plate and strip
EN 10088-3 X1CrNiMoCuN25-25-5
General purposes, semi-finished products, bars, rods, wire, sections and bright products
Can EN 10088-2 X1CrNiMoCuN25-25-5 Be Substituted With EN 10088-3 X1CrNiMoCuN25-25-5?
EN 10088-2 X1CrNiMoCuN25-25-5 and EN 10088-3 X1CrNiMoCuN25-25-5 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
EN 10088-2 X1CrNiMoCuN25-25-5
0 active listings and RFQs →
EN 10088-3 X1CrNiMoCuN25-25-5
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-2 X1CrNiMoCuN25-25-5 and EN 10088-3 X1CrNiMoCuN25-25-5?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-2 X1CrNiMoCuN25-25-5 be substituted with EN 10088-3 X1CrNiMoCuN25-25-5?
EN 10088-2 X1CrNiMoCuN25-25-5 and EN 10088-3 X1CrNiMoCuN25-25-5 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.