EN 10088-2 X1NiCrMoCuN25-20-7 vs ASTM A276/A276M N08925
Close Alternative — 72.9% match
based on chemical composition and mechanical property overlap.
EN 10088-2 X1NiCrMoCuN25-20-7 (EN 10088-2:2014) and ASTM A276/A276M N08925 (ASTM A276/A276M:2017) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-2 X1NiCrMoCuN25-20-7 is typically used for general purposes, hot or cold rolled sheet/plate and strip, while ASTM A276/A276M N08925 is commonly used for stainless steel bars and shapes (hot-finished or cold-finished).
EN 10088-2 X1NiCrMoCuN25-20-7 is defined under European Standard (EN), originating from Europe, while ASTM A276/A276M N08925 is defined under ASTM International, originating from United States.
As per chemical composition, EN 10088-2 X1NiCrMoCuN25-20-7 vs ASTM A276/A276M N08925 is a 92.7% match.
As per mechanical properties, the match is 33.3%.
Combined, this makes them a close alternative overall at 72.9%.
Frequently Compared With EN 10088-2 X1NiCrMoCuN25-20-7:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-2 X1NiCrMoCuN25-20-7
ASTM A276/A276M N08925
Tensile Strength
650-850 MPa
>=600 MPa
Yield Strength
>=300 MPa
>=295 MPa
Elongation
>=40%
>=40%
Condition
Solution annealed (+AT), hot rolled plate, up to 75 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick
Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed)
Hardness
Not specified
<=217 HB
Typical Applications
EN 10088-2 X1NiCrMoCuN25-20-7
General purposes, hot or cold rolled sheet/plate and strip
ASTM A276/A276M N08925
Stainless steel bars and shapes (hot-finished or cold-finished)
Can EN 10088-2 X1NiCrMoCuN25-20-7 Be Substituted With ASTM A276/A276M N08925?
EN 10088-2 X1NiCrMoCuN25-20-7 and ASTM A276/A276M N08925 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
What is the difference between EN 10088-2 X1NiCrMoCuN25-20-7 and ASTM A276/A276M N08925?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-2 X1NiCrMoCuN25-20-7 be substituted with ASTM A276/A276M N08925?
EN 10088-2 X1NiCrMoCuN25-20-7 and ASTM A276/A276M N08925 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.