EN 10088-2 X2CrNbTi20 vs IS 1570 (Part 7) 12Cr12MoVH

Minimal Match — 28.5% match based on chemical composition and mechanical property overlap.

EN 10088-2 X2CrNbTi20 (EN 10088-2:2014) and IS 1570 (Part 7) 12Cr12MoVH (IS 1570 (Part 7):1992) are both steel grades. Both fall under the Stainless Steel category. EN 10088-2 X2CrNbTi20 is typically used for general purposes, hot or cold rolled sheet/plate and strip, while IS 1570 (Part 7) 12Cr12MoVH is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature. EN 10088-2 X2CrNbTi20 is defined under European Standard (EN), originating from Europe, while IS 1570 (Part 7) 12Cr12MoVH is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, EN 10088-2 X2CrNbTi20 vs IS 1570 (Part 7) 12Cr12MoVH is a 42.8% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 28.5%.

Frequently Compared With EN 10088-2 X2CrNbTi20:
ASTM A959 .- GOST 5632 08X18H10 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
42.8%
MECHANICAL MATCH
0%
OVERALL
28.5%
Specifications
Property EN 10088-2 X2CrNbTi20 IS 1570 (Part 7) 12Cr12MoVH
Standard EN 10088-2:2014 IS 1570 (Part 7):1992
Category Stainless Steel Stainless Steel
C (%) <=0.030 0.08-0.16
Si (%) <=1.00 <=0.60
Mn (%) <=1.00 0.40-1.00
P (%) <=0.040 <=0.040
S (%) <=0.015 <=0.035
Cr (%) 18.5-20.5 11.5-13.00
N (%) <=0.030 Not specified
Nb (%) <=1.00 Not specified
Ti (%) <=0.80 Not specified
Ni (%) Not specified <=1.0
Mo (%) Not specified 0.40-0.80
V (%) Not specified 0.10-0.30
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-2 X2CrNbTi20 IS 1570 (Part 7) 12Cr12MoVH
Tensile Strength 430-630 MPa 770-930 MPa
Condition Annealed (+A), cold rolled strip, up to 8 mm thick; Elongation is A80 (under 3 mm) or A (3 mm and over), longitudinal and transverse Bars, forgings, Q+T, thickness up to 150 (first row of Table 3)
Yield Strength >=230 MPa >=585 MPa (0.2 % proof stress)
Elongation >=18% >=15%
Typical Applications
EN 10088-2 X2CrNbTi20
General purposes, hot or cold rolled sheet/plate and strip
IS 1570 (Part 7) 12Cr12MoVH
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
Can EN 10088-2 X2CrNbTi20 Be Substituted With IS 1570 (Part 7) 12Cr12MoVH?
EN 10088-2 X2CrNbTi20 and IS 1570 (Part 7) 12Cr12MoVH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
EN 10088-2 X2CrNbTi20
0 active listings and RFQs →
IS 1570 (Part 7) 12Cr12MoVH
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-2 X2CrNbTi20 and IS 1570 (Part 7) 12Cr12MoVH?
EN 10088-2 X2CrNbTi20 specifies N, Nb, Ti which are not specified for IS 1570 (Part 7) 12Cr12MoVH. IS 1570 (Part 7) 12Cr12MoVH specifies Ni, Mo, V which are not specified for EN 10088-2 X2CrNbTi20.
Can EN 10088-2 X2CrNbTi20 be substituted with IS 1570 (Part 7) 12Cr12MoVH?
EN 10088-2 X2CrNbTi20 and IS 1570 (Part 7) 12Cr12MoVH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.