EN 10088-2 X2CrNiMnMoCuN24-4-3-2 vs EN 10088-3 X2CrNiMnMoCuN24-4-3-2

Close Alternative — 73.3% match based on chemical composition and mechanical property overlap.

EN 10088-2 X2CrNiMnMoCuN24-4-3-2 (EN 10088-2:2014) and EN 10088-3 X2CrNiMnMoCuN24-4-3-2 (EN 10088-3:2014) are both steel grades. Both fall under the Stainless Steel category. EN 10088-2 X2CrNiMnMoCuN24-4-3-2 is typically used for general purposes, hot or cold rolled sheet/plate and strip, while EN 10088-3 X2CrNiMnMoCuN24-4-3-2 is commonly used for general purposes, semi-finished products, bars, rods, wire, sections and bright products. EN 10088-2 X2CrNiMnMoCuN24-4-3-2 is defined under European Standard (EN), originating from Europe, while EN 10088-3 X2CrNiMnMoCuN24-4-3-2 is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10088-2 X2CrNiMnMoCuN24-4-3-2 vs EN 10088-3 X2CrNiMnMoCuN24-4-3-2 is a 100% match. As per mechanical properties, the match is 20%. Combined, this makes them a close alternative overall at 73.3%.

Frequently Compared With EN 10088-2 X2CrNiMnMoCuN24-4-3-2:
ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
100%
MECHANICAL MATCH
20%
OVERALL
73.3%
Specifications
Property EN 10088-2 X2CrNiMnMoCuN24-4-3-2 EN 10088-3 X2CrNiMnMoCuN24-4-3-2
Standard EN 10088-2:2014 EN 10088-3:2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=0.70 <=0.70
Mn (%) 2.50-4.0 2.50-4.0
P (%) <=0.035 <=0.035
S (%) <=0.005 <=0.005
Cr (%) 23.0-25.0 23.0-25.0
Mo (%) 1.00-2.00 1.00-2.00
Ni (%) 3.0-4.5 3.0-4.5
N (%) 0.20-0.30 0.20-0.30
Cu (%) 0.10-0.80 0.10-0.80
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-2 X2CrNiMnMoCuN24-4-3-2 EN 10088-3 X2CrNiMnMoCuN24-4-3-2
Tensile Strength 750-900 MPa 650-900 MPa
Yield Strength >=550 MPa >=450 MPa
Elongation >=20% >=25%
Condition Solution annealed (+AT), cold rolled strip, up to 6.4 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick Solution annealed (+AT), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal), hardness for guidance only
Hardness Not specified <=290 HB
Typical Applications
EN 10088-2 X2CrNiMnMoCuN24-4-3-2
General purposes, hot or cold rolled sheet/plate and strip
EN 10088-3 X2CrNiMnMoCuN24-4-3-2
General purposes, semi-finished products, bars, rods, wire, sections and bright products
Can EN 10088-2 X2CrNiMnMoCuN24-4-3-2 Be Substituted With EN 10088-3 X2CrNiMnMoCuN24-4-3-2?
EN 10088-2 X2CrNiMnMoCuN24-4-3-2 and EN 10088-3 X2CrNiMnMoCuN24-4-3-2 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
EN 10088-2 X2CrNiMnMoCuN24-4-3-2
0 active listings and RFQs →
EN 10088-3 X2CrNiMnMoCuN24-4-3-2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-2 X2CrNiMnMoCuN24-4-3-2 and EN 10088-3 X2CrNiMnMoCuN24-4-3-2?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-2 X2CrNiMnMoCuN24-4-3-2 be substituted with EN 10088-3 X2CrNiMnMoCuN24-4-3-2?
EN 10088-2 X2CrNiMnMoCuN24-4-3-2 and EN 10088-3 X2CrNiMnMoCuN24-4-3-2 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.