Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
EN 10088-2 X2CrNiMo17-12-2 (EN 10088-2:2014) and GOST 5632 06Kh23N28 (GOST 5632-2014) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-2 X2CrNiMo17-12-2 is typically used for general purposes, hot or cold rolled sheet/plate and strip, while GOST 5632 06Kh23N28 is commonly used for furnace components, heat exchangers, high temperature applications.
EN 10088-2 X2CrNiMo17-12-2 is defined under European Standard (EN) (Europe).
As per chemical composition, EN 10088-2 X2CrNiMo17-12-2 vs GOST 5632 06Kh23N28 is a 56% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 35%.
Frequently Compared With EN 10088-2 X2CrNiMo17-12-2:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-2 X2CrNiMo17-12-2
GOST 5632 06Kh23N28
Tensile Strength
530-680 MPa
≥510 MPa
Yield Strength
>=240 MPa
≥196 MPa
Elongation
>=40%
≥35%
Condition
Solution annealed (+AT), cold rolled strip, up to 8 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick
Not specified
Max Service Temp
Not specified
1050°C
Typical Applications
EN 10088-2 X2CrNiMo17-12-2
General purposes, hot or cold rolled sheet/plate and strip
GOST 5632 06Kh23N28
Furnace components, heat exchangers, high temperature applications
Key Differences
EN 10088-2 X2CrNiMo17-12-2 specifies P, S, Mo, N which are not specified for GOST 5632 06Kh23N28.
Can EN 10088-2 X2CrNiMo17-12-2 Be Substituted With GOST 5632 06Kh23N28?
EN 10088-2 X2CrNiMo17-12-2 and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between EN 10088-2 X2CrNiMo17-12-2 and GOST 5632 06Kh23N28?
EN 10088-2 X2CrNiMo17-12-2 specifies P, S, Mo, N which are not specified for GOST 5632 06Kh23N28.
Can EN 10088-2 X2CrNiMo17-12-2 be substituted with GOST 5632 06Kh23N28?
EN 10088-2 X2CrNiMo17-12-2 and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.