EN 10088-2 X2CrNiMoCuWN25-7-4 vs GOST 5632 06Kh23N28

Minimal Match — 31% match based on chemical composition and mechanical property overlap.

EN 10088-2 X2CrNiMoCuWN25-7-4 (EN 10088-2:2014) and GOST 5632 06Kh23N28 (GOST 5632-2014) are both steel grades. Both fall under the Stainless Steel category. EN 10088-2 X2CrNiMoCuWN25-7-4 is typically used for general purposes, hot or cold rolled sheet/plate and strip, while GOST 5632 06Kh23N28 is commonly used for furnace components, heat exchangers, high temperature applications. EN 10088-2 X2CrNiMoCuWN25-7-4 is defined under European Standard (EN) (Europe).

As per chemical composition, EN 10088-2 X2CrNiMoCuWN25-7-4 vs GOST 5632 06Kh23N28 is a 46.5% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 31%.

Frequently Compared With EN 10088-2 X2CrNiMoCuWN25-7-4:
IS 1570 (Part 7) 12Cr12Ni2Mo GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH ASTM A959 .- GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
46.5%
MECHANICAL MATCH
0%
OVERALL
31%
Specifications
Property EN 10088-2 X2CrNiMoCuWN25-7-4 GOST 5632 06Kh23N28
Standard EN 10088-2:2014 GOST 5632-2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 ≤0.06
Si (%) <=1.00 ≤0.80
Mn (%) <=1.00 ≤2.00
P (%) <=0.035 Not specified
S (%) <=0.015 Not specified
Cr (%) 24.0-26.0 22.0–25.0
Mo (%) 3.0-4.0 Not specified
Ni (%) 6.0-8.0 26.0–29.0
N (%) 0.20-0.30 Not specified
Cu (%) 0.50-1.00 Not specified
W (%) 0.50-1.00 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-2 X2CrNiMoCuWN25-7-4 GOST 5632 06Kh23N28
Tensile Strength 730-930 MPa ≥510 MPa
Yield Strength >=530 MPa ≥196 MPa
Elongation >=25% ≥35%
Condition Solution annealed (+AT), hot rolled plate, up to 75 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick Not specified
Max Service Temp Not specified 1050°C
Typical Applications
EN 10088-2 X2CrNiMoCuWN25-7-4
General purposes, hot or cold rolled sheet/plate and strip
GOST 5632 06Kh23N28
Furnace components, heat exchangers, high temperature applications
Key Differences
Can EN 10088-2 X2CrNiMoCuWN25-7-4 Be Substituted With GOST 5632 06Kh23N28?
EN 10088-2 X2CrNiMoCuWN25-7-4 and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
EN 10088-2 X2CrNiMoCuWN25-7-4
No active listings currently.
GOST 5632 06Kh23N28
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 3100–3400 mm (122.05–133.86 in)
On M-EX Right Now
EN 10088-2 X2CrNiMoCuWN25-7-4
0 active listings and RFQs →
GOST 5632 06Kh23N28
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-2 X2CrNiMoCuWN25-7-4 and GOST 5632 06Kh23N28?
EN 10088-2 X2CrNiMoCuWN25-7-4 specifies P, S, Mo, N which are not specified for GOST 5632 06Kh23N28.
Can EN 10088-2 X2CrNiMoCuWN25-7-4 be substituted with GOST 5632 06Kh23N28?
EN 10088-2 X2CrNiMoCuWN25-7-4 and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.