EN 10088-2 X2CrNiMoN25-7-4 vs GOST 5632 08X18H10

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

EN 10088-2 X2CrNiMoN25-7-4 (EN 10088-2:2014) and GOST 5632 08X18H10 (GOST 5632-2014) are both steel grades. Both fall under the Stainless Steel category. EN 10088-2 X2CrNiMoN25-7-4 is typically used for general purposes, hot or cold rolled sheet/plate and strip, while GOST 5632 08X18H10 is commonly used for chemical equipment, food processing, general corrosion resistant applications. EN 10088-2 X2CrNiMoN25-7-4 is defined under European Standard (EN) (Europe).

As per chemical composition, EN 10088-2 X2CrNiMoN25-7-4 vs GOST 5632 08X18H10 is a 52.6% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With EN 10088-2 X2CrNiMoN25-7-4:
ASTM A959 2507 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 GB/T 3280 06Cr19Ni10 EN 10088-1 1.4006 IS 1570 (Part 7) 11Cr17Ni13W3TiH ASTM A959 .- GOST 5632 06Kh23N28 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
52.6%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property EN 10088-2 X2CrNiMoN25-7-4 GOST 5632 08X18H10
Standard EN 10088-2:2014 GOST 5632-2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 ≤0.08
Si (%) <=1.00 ≤0.80
Mn (%) <=2.00 ≤2.00
P (%) <=0.035 ≤0.035
S (%) <=0.015 ≤0.020
Cr (%) 24.0-26.0 17.0–19.0
Mo (%) 3.0-4.5 Not specified
Ni (%) 6.0-8.0 9.0–11.0
N (%) 0.24-0.35 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-2 X2CrNiMoN25-7-4 GOST 5632 08X18H10
Tensile Strength 750-1000 MPa ≥520 MPa
Yield Strength >=550 MPa ≥205 MPa
Elongation >=20% ≥40%
Condition Solution annealed (+AT), cold rolled strip, up to 8 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick Not specified
Typical Applications
EN 10088-2 X2CrNiMoN25-7-4
General purposes, hot or cold rolled sheet/plate and strip
GOST 5632 08X18H10
Chemical equipment, food processing, general corrosion resistant applications
Key Differences
Can EN 10088-2 X2CrNiMoN25-7-4 Be Substituted With GOST 5632 08X18H10?
EN 10088-2 X2CrNiMoN25-7-4 and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
EN 10088-2 X2CrNiMoN25-7-4
No active listings currently.
GOST 5632 08X18H10
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2500–2700 mm (98.43–106.3 in)
On M-EX Right Now
EN 10088-2 X2CrNiMoN25-7-4
0 active listings and RFQs →
GOST 5632 08X18H10
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-2 X2CrNiMoN25-7-4 and GOST 5632 08X18H10?
EN 10088-2 X2CrNiMoN25-7-4 specifies Mo, N which are not specified for GOST 5632 08X18H10.
Can EN 10088-2 X2CrNiMoN25-7-4 be substituted with GOST 5632 08X18H10?
EN 10088-2 X2CrNiMoN25-7-4 and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.