EN 10088-2 X2CrNiMoSi18-5-3 vs GB/T 3280 06Cr19Ni10

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

EN 10088-2 X2CrNiMoSi18-5-3 (EN 10088-2:2014) and GB/T 3280 06Cr19Ni10 (GB/T 3280-2015) are both steel grades. Both fall under the Stainless Steel category. EN 10088-2 X2CrNiMoSi18-5-3 is typically used for general purposes, hot or cold rolled sheet/plate and strip, while GB/T 3280 06Cr19Ni10 is commonly used for used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners.. EN 10088-2 X2CrNiMoSi18-5-3 is defined under European Standard (EN), originating from Europe, while GB/T 3280 06Cr19Ni10 is defined under Guobiao Standards (GB/T), originating from China.

As per chemical composition, EN 10088-2 X2CrNiMoSi18-5-3 vs GB/T 3280 06Cr19Ni10 is a 57.5% match. As per mechanical properties, the match is 1.8%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With EN 10088-2 X2CrNiMoSi18-5-3:
ASTM A959 .- GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
57.5%
MECHANICAL MATCH
1.8%
OVERALL
35%
Specifications
Property EN 10088-2 X2CrNiMoSi18-5-3 GB/T 3280 06Cr19Ni10
Standard EN 10088-2:2014 GB/T 3280-2015
Category Stainless Steel Stainless Steel
C (%) <=0.030 0.08 max
Si (%) 1.40-2.00 1.00 max
Mn (%) 1.20-2.00 2.00 max
P (%) <=0.035 0.045 max
S (%) <=0.015 0.030 max
Cr (%) 18.0-19.0 18.00-20.00
Mo (%) 2.50-3.0 Not specified
Ni (%) 4.5-5.2 8.00-11.00
N (%) 0.05-0.10 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-2 X2CrNiMoSi18-5-3 GB/T 3280 06Cr19Ni10
Tensile Strength 700-900 MPa 520-720 MPa
Yield Strength >=450 MPa 205-310 MPa
Elongation >=25% 40-60%
Condition Solution annealed (+AT), cold rolled strip, up to 8 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick Not specified
Hardness Not specified 187 HB max
Typical Applications
EN 10088-2 X2CrNiMoSi18-5-3
General purposes, hot or cold rolled sheet/plate and strip
GB/T 3280 06Cr19Ni10
Used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners.
Key Differences
Can EN 10088-2 X2CrNiMoSi18-5-3 Be Substituted With GB/T 3280 06Cr19Ni10?
EN 10088-2 X2CrNiMoSi18-5-3 and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
EN 10088-2 X2CrNiMoSi18-5-3
No active listings currently.
GB/T 3280 06Cr19Ni10
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2900–3300 mm (114.17–129.92 in)
On M-EX Right Now
EN 10088-2 X2CrNiMoSi18-5-3
0 active listings and RFQs →
GB/T 3280 06Cr19Ni10
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-2 X2CrNiMoSi18-5-3 and GB/T 3280 06Cr19Ni10?
EN 10088-2 X2CrNiMoSi18-5-3 specifies Mo, N which are not specified for GB/T 3280 06Cr19Ni10.
Can EN 10088-2 X2CrNiMoSi18-5-3 be substituted with GB/T 3280 06Cr19Ni10?
EN 10088-2 X2CrNiMoSi18-5-3 and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.