Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C
Si
Mn
P
S
Cr
Ni
N
<=0.030
<=1.00
<=2.00
<=0.045
<=0.015
16.5-18.5
6.0-8.0
0.10-0.20
Mechanical Properties
Tensile Strength
650-850 MPa
Yield Strength
>=350 MPa
Elongation
>=35%
Condition
Solution annealed (+AT), cold rolled strip, up to 8 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick
More data from EN 10088-2:2014
From the standard
Mechanical properties by product form and thickness3 product forms
Product form
Max thickness (mm)
Rp0.2 min (MPa)
Rp1.0 min (MPa)
Rm (MPa)
A80 min, under 3 mm thick (%)
A min, 3 mm and over (%)
Cold rolled strip
8
350
380
650 to 850
35
40
Hot rolled strip
13.5
330
370
650 to 850
35
40
Hot rolled plate
75
330
370
630 to 830
45
45
Solution annealed condition; proof strength and elongation are minimum transverse values.
Source: EN 10088-2:2014, Table 7
Impact energy KV2 (ISO-V)2 rows
Product form
Max thickness (mm)
KV2 longitudinal, min (J)
KV2 transverse, min (J)
Hot rolled strip
13.5
90
60
Hot rolled plate
75
90
60
Applies to products more than 10 mm thick, ISO-V notch, room temperature.
Source: EN 10088-2:2014, Table 7
Proof strength at elevated temperature10 temperatures
Temperature (deg C)
Rp0.2 min (MPa)
Rp1.0 min (MPa)
100
265
300
150
200
235
200
185
215
250
180
210
300
170
200
350
165
195
400
-
-
450
-
-
500
-
-
550
-
-
Minimum values, solution annealed (+AT).
Source: EN 10088-2:2014, Table 12
Hot forming and solution annealingguideline temperatures
Hot forming temperature
1150 to 850 deg C
Cooling after hot forming
air
Heat treatment symbol
+AT
Solution annealing temperature
1020 to 1100 deg C
Cooling after solution annealing
water, air
Informative guideline; cooling must be rapid enough to avoid intergranular corrosion.
Source: EN 10088-2:2014, Table A.1
Cold worked condition levels (process route 2H)cold worked levels
Available tensile strength levels
+C850 (850 to 1000 MPa); +C1000 (1000 to 1150 MPa)
Available 0.2% proof strength levels
+CP500 (500 to 700 MPa); +CP700 (700 to 900 MPa)
Only one parameter (tensile strength or proof strength) can be specified in the order.
Source: EN 10088-2:2014, Table 19 and 20
Active EN 10088-2:2014 X2CrNiN18-7 Listings on M-EX (For Sale)