EN 10088-2 X2CrNiN23-4 vs EN 10088-2 X2CrNiCuN23-4

Close Alternative — 83.7% match based on chemical composition and mechanical property overlap.

EN 10088-2 X2CrNiN23-4 (EN 10088-2:2014) and EN 10088-2 X2CrNiCuN23-4 (EN 10088-2:2014) are both steel grades. Both fall under the Stainless Steel category. EN 10088-2 X2CrNiN23-4 is typically used for general purposes, hot or cold rolled sheet/plate and strip, while EN 10088-2 X2CrNiCuN23-4 is commonly used for general purposes, hot or cold rolled sheet/plate and strip. EN 10088-2 X2CrNiN23-4 is defined under European Standard (EN), originating from Europe, while EN 10088-2 X2CrNiCuN23-4 is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10088-2 X2CrNiN23-4 vs EN 10088-2 X2CrNiCuN23-4 is a 95.6% match. As per mechanical properties, the match is 60%. Combined, this makes them a close alternative overall at 83.7%.

Frequently Compared With EN 10088-2 X2CrNiN23-4:
ASTM A959 2304 ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
95.6%
MECHANICAL MATCH
60%
OVERALL
83.7%
Specifications
Property EN 10088-2 X2CrNiN23-4 EN 10088-2 X2CrNiCuN23-4
Standard EN 10088-2:2014 EN 10088-2:2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Mn (%) <=2.00 <=2.00
P (%) <=0.035 <=0.035
S (%) <=0.015 <=0.015
Cr (%) 22.0-24.5 22.0-24.0
Mo (%) 0.10-0.60 0.10-0.60
Ni (%) 3.5-5.5 3.5-5.5
N (%) 0.05-0.20 0.05-0.20
Cu (%) 0.10-0.60 1.00-3.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-2 X2CrNiN23-4 EN 10088-2 X2CrNiCuN23-4
Tensile Strength 650-850 MPa 600-850 MPa
Yield Strength >=450 MPa >=420 MPa
Elongation >=20% >=20%
Condition Solution annealed (+AT), cold rolled strip, up to 8 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick Solution annealed (+AT), cold rolled strip, up to 8 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick
Typical Applications
EN 10088-2 X2CrNiN23-4
General purposes, hot or cold rolled sheet/plate and strip
EN 10088-2 X2CrNiCuN23-4
General purposes, hot or cold rolled sheet/plate and strip
Can EN 10088-2 X2CrNiN23-4 Be Substituted With EN 10088-2 X2CrNiCuN23-4?
EN 10088-2 X2CrNiN23-4 and EN 10088-2 X2CrNiCuN23-4 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
EN 10088-2 X2CrNiN23-4
0 active listings and RFQs →
EN 10088-2 X2CrNiCuN23-4
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-2 X2CrNiN23-4 and EN 10088-2 X2CrNiCuN23-4?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-2 X2CrNiN23-4 be substituted with EN 10088-2 X2CrNiCuN23-4?
EN 10088-2 X2CrNiN23-4 and EN 10088-2 X2CrNiCuN23-4 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.