EN 10088-2 X2CrSiTi15 vs GB/T 3280 06Cr19Ni10

Minimal Match — 34.3% match based on chemical composition and mechanical property overlap.

EN 10088-2 X2CrSiTi15 (EN 10088-2:2014) and GB/T 3280 06Cr19Ni10 (GB/T 3280-2015) are both steel grades. Both fall under the Stainless Steel category. EN 10088-2 X2CrSiTi15 is typically used for general purposes, hot or cold rolled sheet/plate and strip, while GB/T 3280 06Cr19Ni10 is commonly used for used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners.. EN 10088-2 X2CrSiTi15 is defined under European Standard (EN), originating from Europe, while GB/T 3280 06Cr19Ni10 is defined under Guobiao Standards (GB/T), originating from China.

As per chemical composition, EN 10088-2 X2CrSiTi15 vs GB/T 3280 06Cr19Ni10 is a 48.5% match. As per mechanical properties, the match is 5.9%. Combined, this makes them a minimal match overall at 34.3%.

Frequently Compared With EN 10088-2 X2CrSiTi15:
IS 1570 (Part 7) 12Cr12Ni2Mo GOST 5632 06Kh23N28 EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr12MoVH ASTM A959 .- GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
48.5%
MECHANICAL MATCH
5.9%
OVERALL
34.3%
Specifications
Property EN 10088-2 X2CrSiTi15 GB/T 3280 06Cr19Ni10
Standard EN 10088-2:2014 GB/T 3280-2015
Category Stainless Steel Stainless Steel
C (%) <=0.030 0.08 max
Si (%) 0.20-1.50 1.00 max
Mn (%) <=1.00 2.00 max
P (%) <=0.050 0.045 max
S (%) <=0.050 0.030 max
Cr (%) 13.0-16.0 18.00-20.00
Mo (%) <=0.50 Not specified
Ni (%) <=0.50 8.00-11.00
Nb (%) <=0.50 Not specified
Ti (%) <=0.80 Not specified
Al (%) <=1.50 Not specified
Cu (%) <=0.50 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-2 X2CrSiTi15 GB/T 3280 06Cr19Ni10
Tensile Strength 380-580 MPa 520-720 MPa
Condition Annealed (+A), cold rolled strip, up to 8 mm thick; Elongation is A80 (under 3 mm) or A (3 mm and over), longitudinal and transverse Not specified
Yield Strength >=210 MPa 205-310 MPa
Elongation >=20% 40-60%
Hardness Not specified 187 HB max
Typical Applications
EN 10088-2 X2CrSiTi15
General purposes, hot or cold rolled sheet/plate and strip
GB/T 3280 06Cr19Ni10
Used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners.
Key Differences
Can EN 10088-2 X2CrSiTi15 Be Substituted With GB/T 3280 06Cr19Ni10?
EN 10088-2 X2CrSiTi15 and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
EN 10088-2 X2CrSiTi15
No active listings currently.
GB/T 3280 06Cr19Ni10
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2900–3300 mm (114.17–129.92 in)
On M-EX Right Now
EN 10088-2 X2CrSiTi15
0 active listings and RFQs →
GB/T 3280 06Cr19Ni10
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-2 X2CrSiTi15 and GB/T 3280 06Cr19Ni10?
EN 10088-2 X2CrSiTi15 specifies Mo, Nb, Ti, Al which are not specified for GB/T 3280 06Cr19Ni10.
Can EN 10088-2 X2CrSiTi15 be substituted with GB/T 3280 06Cr19Ni10?
EN 10088-2 X2CrSiTi15 and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.