EN 10088-2 X2CrTi12 vs IS 1570 (Part 7) 11Cr17Ni13W3TiH
Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
EN 10088-2 X2CrTi12 (EN 10088-2:2014) and IS 1570 (Part 7) 11Cr17Ni13W3TiH (IS 1570 (Part 7):1992) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-2 X2CrTi12 is typically used for general purposes, hot or cold rolled sheet/plate and strip, while IS 1570 (Part 7) 11Cr17Ni13W3TiH is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature.
EN 10088-2 X2CrTi12 is defined under European Standard (EN), originating from Europe, while IS 1570 (Part 7) 11Cr17Ni13W3TiH is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, EN 10088-2 X2CrTi12 vs IS 1570 (Part 7) 11Cr17Ni13W3TiH is a 57.1% match.
As per mechanical properties, the match is 33.3%.
Combined, this makes them a minimal match overall at 35%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-2 X2CrTi12
IS 1570 (Part 7) 11Cr17Ni13W3TiH
Tensile Strength
380-560 MPa
600-800 MPa
Condition
Annealed (+A), cold rolled strip, up to 8 mm thick; Elongation is A80 (under 3 mm) or A (3 mm and over), longitudinal and transverse
Bars, forgings, pipes, hot cold worked, thickness up to 60 (first row of Table 3)
Yield Strength
>=210 MPa
>=390 MPa (0.2 % proof stress)
Elongation
>=25%
>=25%
Typical Applications
EN 10088-2 X2CrTi12
General purposes, hot or cold rolled sheet/plate and strip
IS 1570 (Part 7) 11Cr17Ni13W3TiH
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
IS 1570 (Part 7) 11Cr17Ni13W3TiH specifies Ni, W, B which are not specified for EN 10088-2 X2CrTi12.
Can EN 10088-2 X2CrTi12 Be Substituted With IS 1570 (Part 7) 11Cr17Ni13W3TiH?
EN 10088-2 X2CrTi12 and IS 1570 (Part 7) 11Cr17Ni13W3TiH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between EN 10088-2 X2CrTi12 and IS 1570 (Part 7) 11Cr17Ni13W3TiH?
IS 1570 (Part 7) 11Cr17Ni13W3TiH specifies Ni, W, B which are not specified for EN 10088-2 X2CrTi12.
Can EN 10088-2 X2CrTi12 be substituted with IS 1570 (Part 7) 11Cr17Ni13W3TiH?
EN 10088-2 X2CrTi12 and IS 1570 (Part 7) 11Cr17Ni13W3TiH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.