Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
EN 10088-2 X39Cr13 (EN 10088-2:2014) and GOST 5632 06Kh23N28 (GOST 5632-2014) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-2 X39Cr13 is typically used for general purposes, hot or cold rolled sheet/plate and strip, while GOST 5632 06Kh23N28 is commonly used for furnace components, heat exchangers, high temperature applications.
EN 10088-2 X39Cr13 is defined under European Standard (EN) (Europe).
As per chemical composition, EN 10088-2 X39Cr13 vs GOST 5632 06Kh23N28 is a 61.9% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 35%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-2 X39Cr13
GOST 5632 06Kh23N28
Tensile Strength
<=760 MPa
≥510 MPa
Elongation
>=12%
≥35%
Hardness
<=240 HB
Not specified
Condition
Annealed (+A), cold rolled strip, up to 8 mm thick
Not specified
Yield Strength
Not specified
≥196 MPa
Max Service Temp
Not specified
1050°C
Typical Applications
EN 10088-2 X39Cr13
General purposes, hot or cold rolled sheet/plate and strip
GOST 5632 06Kh23N28
Furnace components, heat exchangers, high temperature applications
Key Differences
EN 10088-2 X39Cr13 specifies P, S which are not specified for GOST 5632 06Kh23N28.
GOST 5632 06Kh23N28 specifies Ni which is not specified for EN 10088-2 X39Cr13.
Can EN 10088-2 X39Cr13 Be Substituted With GOST 5632 06Kh23N28?
EN 10088-2 X39Cr13 and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between EN 10088-2 X39Cr13 and GOST 5632 06Kh23N28?
EN 10088-2 X39Cr13 specifies P, S which are not specified for GOST 5632 06Kh23N28. GOST 5632 06Kh23N28 specifies Ni which is not specified for EN 10088-2 X39Cr13.
Can EN 10088-2 X39Cr13 be substituted with GOST 5632 06Kh23N28?
EN 10088-2 X39Cr13 and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.