EN 10088-2 X39CrMo17-1 vs BS 970 (Part 1) 416S37

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

EN 10088-2 X39CrMo17-1 (EN 10088-2:2014) and BS 970 (Part 1) 416S37 (BS 970 (Part 1):1991) are both steel grades. Both fall under the Stainless Steel category. EN 10088-2 X39CrMo17-1 is typically used for general purposes, hot or cold rolled sheet/plate and strip, while BS 970 (Part 1) 416S37 is commonly used for ferritic and martensitic stainless and heat resisting steel (section five). EN 10088-2 X39CrMo17-1 is defined under European Standard (EN), originating from Europe, while BS 970 (Part 1) 416S37 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, EN 10088-2 X39CrMo17-1 vs BS 970 (Part 1) 416S37 is a 71.3% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With EN 10088-2 X39CrMo17-1:
ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
71.3%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property EN 10088-2 X39CrMo17-1 BS 970 (Part 1) 416S37
Standard EN 10088-2:2014 BS 970 (Part 1):1991
Category Stainless Steel Stainless Steel
C (%) 0.33-0.45 0.20-0.28
Si (%) <=1.00 <=1.0
Mn (%) <=1.50 <=1.5
P (%) <=0.040 <=0.060
S (%) <=0.015 0.15-0.35
Cr (%) 15.5-17.5 12.0-14.0
Mo (%) 0.80-1.30 <=0.60
Ni (%) <=1.00 <=1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-2 X39CrMo17-1 BS 970 (Part 1) 416S37
Tensile Strength <=900 MPa Not specified
Elongation >=12% Not specified
Hardness <=280 HB Not specified
Condition Annealed (+A), cold rolled strip, up to 8 mm thick Not specified
Typical Applications
EN 10088-2 X39CrMo17-1
General purposes, hot or cold rolled sheet/plate and strip
BS 970 (Part 1) 416S37
Ferritic and martensitic stainless and heat resisting steel (section five)
Can EN 10088-2 X39CrMo17-1 Be Substituted With BS 970 (Part 1) 416S37?
EN 10088-2 X39CrMo17-1 and BS 970 (Part 1) 416S37 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
EN 10088-2 X39CrMo17-1
0 active listings and RFQs →
BS 970 (Part 1) 416S37
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-2 X39CrMo17-1 and BS 970 (Part 1) 416S37?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-2 X39CrMo17-1 be substituted with BS 970 (Part 1) 416S37?
EN 10088-2 X39CrMo17-1 and BS 970 (Part 1) 416S37 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.