EN 10088-2:2014 X3CrNb17 Steel: Specifications & Listings

EN 10088-2:2014 X3CrNb17: X3CrNb17: ferritic corrosion resisting stainless steel, material number 1.4511. Specified in EN 10088-2:2014.

Category: Stainless Steel
Grade Details
GradeEN 10088-2:2014 X3CrNb17
Standard EN 10088-2:2014
ApplicationsGeneral purposes, hot or cold rolled sheet/plate and strip
Equivalent / Similar Grades
Grade Standard Region Live on M-EX
EN 10088-1 X3CrTi17 EN 10088-1:2014 Europe (CEN) No activity yet
EN 10088-1 X3CrNb17 EN 10088-1:2014 Europe (CEN) No activity yet
EN 10088-1 X2CrNbTi20 EN 10088-1:2014 Europe (CEN) No activity yet
EN 10088-1 X2CrNbZr17 EN 10088-1:2014 Europe (CEN) No activity yet
EN 10088-1 X3CrAlTi18-2 EN 10088-1:2014 Europe (CEN) No activity yet
EN 10088-2 X3CrTi17 EN 10088-2:2014 Europe No activity yet
EN 10088-2 X2CrNbZr17 EN 10088-2:2014 Europe No activity yet
Grade ComparisonCompare With a Specific Grade →
Grade Standard Match
EN 10088-1 X3CrTi17 EN 10088-1:2014 Strong Match
EN 10088-1 X3CrNb17 EN 10088-1:2014 Strong Match
EN 10088-1 X3CrTi17 EN 10088-1:2023 Strong Match
EN 10088-1 X3CrNb17 EN 10088-1:2023 Strong Match
EN 10088-2 X3CrTi17 EN 10088-2:2014 Strong Match
EN 10088-1 X2CrNbZr17 EN 10088-1:2014 Strong Match
EN 10088-2 X2CrNbZr17 EN 10088-2:2014 Strong Match
EN 10088-1 X2CrNbZr17 EN 10088-1:2023 Strong Match
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C Si Mn P S Cr Nb
<=0.05 <=1.00 <=1.00 <=0.040 <=0.015 16.0-18.0 <=1.00
Mechanical Properties
Tensile Strength 420-600 MPa
Condition Annealed (+A), cold rolled strip, up to 8 mm thick; Elongation is A80 (under 3 mm) or A (3 mm and over), longitudinal and transverse
Yield Strength >=230 MPa
Elongation >=23%

More data from EN 10088-2:2014

From the standard
Mechanical properties by product form and thickness 1 product form
Product formMax thickness (mm)Rp0.2 longitudinal, min (MPa)Rp0.2 transverse, min (MPa)Rm (MPa)A80 min, under 3 mm thick (%)A min, 3 mm and over (%)
Cold rolled strip8230240420 to 6002323
Annealed condition; one elongation value is printed for both thickness classes.
Source: EN 10088-2:2014, Table 9
Proof strength at elevated temperature 7 temperatures
Temperature (deg C)Rp0.2 min (MPa)
100230
150220
200205
250190
300180
350165
400-
Minimum values, annealed (+A).
Source: EN 10088-2:2014, Table 14
Hot forming and annealing guideline temperatures
Hot forming temperature
1100 to 800 deg C
Cooling after hot forming
air
Heat treatment symbol
+A
Annealing temperature
790 to 850 deg C
Cooling after annealing
air, water
Informative guideline.
Source: EN 10088-2:2014, Table A.3

Active EN 10088-2:2014 X3CrNb17 Listings on M-EX (For Sale)

+ Create a Listing for this grade

No active EN 10088-2:2014 X3CrNb17 listings at this time.

Register for Alerts

Buyer RFQs for EN 10088-2:2014 X3CrNb17

+ Post an RFQ for this grade

No open buyer requirements for EN 10088-2:2014 X3CrNb17 at this time.

Register for Alerts