Related Material — 67.6% match based on chemical composition and mechanical property overlap.

EN 10088-2 X3CrNiMo13-4 (EN 10088-2:2014) and ASTM A959 S32950 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. EN 10088-2 X3CrNiMo13-4 is typically used for general purposes, hot or cold rolled sheet/plate and strip, while ASTM A959 S32950 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). EN 10088-2 X3CrNiMo13-4 is defined under European Standard (EN), originating from Europe, while ASTM A959 S32950 is defined under ASTM International, originating from United States.

As per chemical composition, EN 10088-2 X3CrNiMo13-4 vs ASTM A959 S32950 is a 67.6% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 67.6%.

Frequently Compared With EN 10088-2 X3CrNiMo13-4:
ASTM A959 25-4-4 ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
67.6%
MECHANICAL MATCH
No shared data
OVERALL
67.6%
Specifications
Property EN 10088-2 X3CrNiMo13-4 ASTM A959 S32950
Standard EN 10088-2:2014 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.05 <=0.030
Si (%) <=0.70 <=0.60
Mn (%) <=1.50 <=2.00
P (%) <=0.040 <=0.035
S (%) <=0.015 <=0.010
Cr (%) 12.0-14.0 26.0-29.0
Mo (%) 0.30-0.70 1.00-2.50
Ni (%) 3.5-4.5 3.5-5.2
N (%) >=0.020 0.15-0.35
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-2 X3CrNiMo13-4 ASTM A959 S32950
Tensile Strength 780-980 MPa Not specified
Yield Strength >=630 MPa Not specified
Elongation >=15% Not specified
Condition Quenched and tempered (+QT780), hot rolled plate, up to 75 mm thick Not specified
Typical Applications
EN 10088-2 X3CrNiMo13-4
General purposes, hot or cold rolled sheet/plate and strip
ASTM A959 S32950
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Can EN 10088-2 X3CrNiMo13-4 Be Substituted With ASTM A959 S32950?
EN 10088-2 X3CrNiMo13-4 and ASTM A959 S32950 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
EN 10088-2 X3CrNiMo13-4
0 active listings and RFQs →
ASTM A959 S32950
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-2 X3CrNiMo13-4 and ASTM A959 S32950?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-2 X3CrNiMo13-4 be substituted with ASTM A959 S32950?
EN 10088-2 X3CrNiMo13-4 and ASTM A959 S32950 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.