EN 10088-2 X5CrNiCuNb16-4 vs IS 6603 X05Cr16Ni4CuNb
Related Material — 65.7% match
based on chemical composition and mechanical property overlap.
EN 10088-2 X5CrNiCuNb16-4 (EN 10088-2:2014) and IS 6603 X05Cr16Ni4CuNb (IS 6603:2024) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-2 X5CrNiCuNb16-4 is typically used for general purposes, hot or cold rolled sheet/plate and strip, while IS 6603 X05Cr16Ni4CuNb is commonly used for general purposes, semi-finished products, bars, wire rods and bright bars.
EN 10088-2 X5CrNiCuNb16-4 is defined under European Standard (EN), originating from Europe, while IS 6603 X05Cr16Ni4CuNb is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, EN 10088-2 X5CrNiCuNb16-4 vs IS 6603 X05Cr16Ni4CuNb is a 98.6% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a related material overall at 65.7%.
Frequently Compared With EN 10088-2 X5CrNiCuNb16-4:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-2 X5CrNiCuNb16-4
IS 6603 X05Cr16Ni4CuNb
Tensile Strength
<=1275 MPa
<=1200 MPa
Elongation
>=5%
Not specified
Condition
Solution annealed (+AT, delivery condition), cold rolled strip, up to 8 mm thick
Solution annealed (+AT), conditions 1C, 1E, 1D, 1X, 1G and 2D; hardness as printed
Hardness
Not specified
<=363 HB
Typical Applications
EN 10088-2 X5CrNiCuNb16-4
General purposes, hot or cold rolled sheet/plate and strip
IS 6603 X05Cr16Ni4CuNb
General purposes, semi-finished products, bars, wire rods and bright bars
Can EN 10088-2 X5CrNiCuNb16-4 Be Substituted With IS 6603 X05Cr16Ni4CuNb?
EN 10088-2 X5CrNiCuNb16-4 and IS 6603 X05Cr16Ni4CuNb share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between EN 10088-2 X5CrNiCuNb16-4 and IS 6603 X05Cr16Ni4CuNb?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-2 X5CrNiCuNb16-4 be substituted with IS 6603 X05Cr16Ni4CuNb?
EN 10088-2 X5CrNiCuNb16-4 and IS 6603 X05Cr16Ni4CuNb share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.