Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
EN 10088-2 X6CrAl13 (EN 10088-2:2014) and EN 10088-1 1.4845 (EN 10088-1:2014) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-2 X6CrAl13 is typically used for general purposes, hot or cold rolled sheet/plate and strip, while EN 10088-1 1.4845 is commonly used for furnace parts, heat exchangers, kiln components.
EN 10088-2 X6CrAl13 is defined under European Standard (EN), originating from Europe, while EN 10088-1 1.4845 is defined under European Standard (EN), originating from Europe.
As per chemical composition, EN 10088-2 X6CrAl13 vs EN 10088-1 1.4845 is a 64.4% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 35%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-2 X6CrAl13
EN 10088-1 1.4845
Tensile Strength
400-600 MPa
≥515 MPa
Condition
Annealed (+A), cold rolled strip, up to 8 mm thick; Elongation is A80 (under 3 mm) or A (3 mm and over), longitudinal and transverse
Not specified
Yield Strength
>=230 MPa
≥205 MPa
Elongation
>=17%
≥40%
Max Service Temp
Not specified
1100°C continuous
Typical Applications
EN 10088-2 X6CrAl13
General purposes, hot or cold rolled sheet/plate and strip
EN 10088-1 1.4845
Furnace parts, heat exchangers, kiln components
Key Differences
EN 10088-2 X6CrAl13 specifies P, S, Al which are not specified for EN 10088-1 1.4845.
EN 10088-1 1.4845 specifies Ni which is not specified for EN 10088-2 X6CrAl13.
Can EN 10088-2 X6CrAl13 Be Substituted With EN 10088-1 1.4845?
EN 10088-2 X6CrAl13 and EN 10088-1 1.4845 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between EN 10088-2 X6CrAl13 and EN 10088-1 1.4845?
EN 10088-2 X6CrAl13 specifies P, S, Al which are not specified for EN 10088-1 1.4845. EN 10088-1 1.4845 specifies Ni which is not specified for EN 10088-2 X6CrAl13.
Can EN 10088-2 X6CrAl13 be substituted with EN 10088-1 1.4845?
EN 10088-2 X6CrAl13 and EN 10088-1 1.4845 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.