EN 10088-2 X6CrNiMoNb17-12-2 vs BS 970 (Part 1) 316S31

Strong Match — 92.3% match based on chemical composition and mechanical property overlap.

EN 10088-2 X6CrNiMoNb17-12-2 (EN 10088-2:2014) and BS 970 (Part 1) 316S31 (BS 970 (Part 1):1983) are both steel grades. Both fall under the Stainless Steel category. EN 10088-2 X6CrNiMoNb17-12-2 is typically used for general purposes, hot or cold rolled sheet/plate and strip, while BS 970 (Part 1) 316S31 is commonly used for austenitic stainless and heat resisting steel for mechanical and allied engineering purposes (table 14, with table 15 for the cold drawn condition).. EN 10088-2 X6CrNiMoNb17-12-2 is defined under European Standard (EN), originating from Europe, while BS 970 (Part 1) 316S31 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, EN 10088-2 X6CrNiMoNb17-12-2 vs BS 970 (Part 1) 316S31 is a 92.3% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 92.3%.

Frequently Compared With EN 10088-2 X6CrNiMoNb17-12-2:
ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
92.3%
MECHANICAL MATCH
No shared data
OVERALL
92.3%
Specifications
Property EN 10088-2 X6CrNiMoNb17-12-2 BS 970 (Part 1) 316S31
Standard EN 10088-2:2014 BS 970 (Part 1):1983
Category Stainless Steel Stainless Steel
C (%) <=0.08 <=0.07
Si (%) <=1.00 <=1.0
Mn (%) <=2.00 <=2.0
P (%) <=0.045 <=0.045
S (%) <=0.015 <=0.030
Cr (%) 16.5-18.5 16.5-18.5
Mo (%) 2.00-2.50 2.00-2.50
Ni (%) 10.5-13.5 10.5-13.5
Nb (%) <=1.00 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-2 X6CrNiMoNb17-12-2 BS 970 (Part 1) 316S31
Tensile Strength 520-720 MPa Not specified
Yield Strength >=220 MPa Not specified
Elongation >=40% Not specified
Condition Solution annealed (+AT), hot rolled plate, up to 75 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick Not specified
Typical Applications
EN 10088-2 X6CrNiMoNb17-12-2
General purposes, hot or cold rolled sheet/plate and strip
BS 970 (Part 1) 316S31
Austenitic stainless and heat resisting steel for mechanical and allied engineering purposes (Table 14, with Table 15 for the cold drawn condition).
Key Differences
Can EN 10088-2 X6CrNiMoNb17-12-2 Be Substituted With BS 970 (Part 1) 316S31?
EN 10088-2 X6CrNiMoNb17-12-2 and BS 970 (Part 1) 316S31 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 1) 316S31 is often considered as a substitute for EN 10088-2 X6CrNiMoNb17-12-2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
EN 10088-2 X6CrNiMoNb17-12-2
0 active listings and RFQs →
BS 970 (Part 1) 316S31
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-2 X6CrNiMoNb17-12-2 and BS 970 (Part 1) 316S31?
EN 10088-2 X6CrNiMoNb17-12-2 specifies Nb which is not specified for BS 970 (Part 1) 316S31.
Can EN 10088-2 X6CrNiMoNb17-12-2 be substituted with BS 970 (Part 1) 316S31?
EN 10088-2 X6CrNiMoNb17-12-2 and BS 970 (Part 1) 316S31 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 1) 316S31 is often considered as a substitute for EN 10088-2 X6CrNiMoNb17-12-2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.