EN 10088-2 X6CrNiTi12 vs ASTM A959 S40800

Close Alternative — 77.1% match based on chemical composition and mechanical property overlap.

EN 10088-2 X6CrNiTi12 (EN 10088-2:2014) and ASTM A959 S40800 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. EN 10088-2 X6CrNiTi12 is typically used for general purposes, hot or cold rolled sheet/plate and strip, while ASTM A959 S40800 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). EN 10088-2 X6CrNiTi12 is defined under European Standard (EN), originating from Europe, while ASTM A959 S40800 is defined under ASTM International, originating from United States.

As per chemical composition, EN 10088-2 X6CrNiTi12 vs ASTM A959 S40800 is a 77.1% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 77.1%.

Frequently Compared With EN 10088-2 X6CrNiTi12:
ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
77.1%
MECHANICAL MATCH
No shared data
OVERALL
77.1%
Specifications
Property EN 10088-2 X6CrNiTi12 ASTM A959 S40800
Standard EN 10088-2:2014 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.08 <=0.08
Si (%) <=0.70 <=1.00
Mn (%) <=1.50 <=1.00
P (%) <=0.040 <=0.045
S (%) <=0.015 <=0.045
Cr (%) 10.5-12.5 11.5-13.0
Ni (%) 0.50-1.50 <=0.80
Ti (%) 0.05-0.35 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-2 X6CrNiTi12 ASTM A959 S40800
Tensile Strength 450-650 MPa Not specified
Condition Annealed (+A), cold rolled strip, up to 8 mm thick; Elongation is A80 (under 3 mm) or A (3 mm and over), longitudinal and transverse Not specified
Yield Strength >=280 MPa Not specified
Elongation >=23% Not specified
Typical Applications
EN 10088-2 X6CrNiTi12
General purposes, hot or cold rolled sheet/plate and strip
ASTM A959 S40800
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can EN 10088-2 X6CrNiTi12 Be Substituted With ASTM A959 S40800?
EN 10088-2 X6CrNiTi12 and ASTM A959 S40800 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
EN 10088-2 X6CrNiTi12
0 active listings and RFQs →
ASTM A959 S40800
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-2 X6CrNiTi12 and ASTM A959 S40800?
EN 10088-2 X6CrNiTi12 specifies Ti which is not specified for ASTM A959 S40800.
Can EN 10088-2 X6CrNiTi12 be substituted with ASTM A959 S40800?
EN 10088-2 X6CrNiTi12 and ASTM A959 S40800 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.