Strong Match — 97.6% match
based on chemical composition and mechanical property overlap.
EN 10088-2 X7CrNiAl17-7 (EN 10088-2:2014) and JIS G4305 SUS631 (JIS G4305:2012) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-2 X7CrNiAl17-7 is typically used for general purposes, hot or cold rolled sheet/plate and strip, while JIS G4305 SUS631 is commonly used for cold-rolled stainless steel plates, sheet and strip.
EN 10088-2 X7CrNiAl17-7 is defined under European Standard (EN), originating from Europe, while JIS G4305 SUS631 is defined under Japanese Industrial Standards (JIS), originating from Japan.
As per chemical composition, EN 10088-2 X7CrNiAl17-7 vs JIS G4305 SUS631 is a 96.5% match.
As per mechanical properties, the match is 100%.
Combined, this makes them a strong match overall at 97.6%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-2 X7CrNiAl17-7
JIS G4305 SUS631
Tensile Strength
<=1030 MPa
<=1030 MPa
Elongation
>=19%
Not specified
Condition
Solution annealed (+AT, delivery condition), cold rolled strip, up to 8 mm thick
Solution heat treated plate and strip; proof strength applies only when specified by the purchaser
Yield Strength
Not specified
<=380 MPa
Hardness
Not specified
<=192 HB
Typical Applications
EN 10088-2 X7CrNiAl17-7
General purposes, hot or cold rolled sheet/plate and strip
JIS G4305 SUS631
Cold-rolled stainless steel plates, sheet and strip
Can EN 10088-2 X7CrNiAl17-7 Be Substituted With JIS G4305 SUS631?
EN 10088-2 X7CrNiAl17-7 and JIS G4305 SUS631 overlap closely enough on chemistry and mechanical properties that JIS G4305 SUS631 is often considered as a substitute for EN 10088-2 X7CrNiAl17-7 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between EN 10088-2 X7CrNiAl17-7 and JIS G4305 SUS631?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-2 X7CrNiAl17-7 be substituted with JIS G4305 SUS631?
EN 10088-2 X7CrNiAl17-7 and JIS G4305 SUS631 overlap closely enough on chemistry and mechanical properties that JIS G4305 SUS631 is often considered as a substitute for EN 10088-2 X7CrNiAl17-7 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.