EN 10088-2 X8CrMnCuN17-8-3 vs EN 10088-1 X8CrMnCuN17-8-3

Strong Match — 100% match based on chemical composition and mechanical property overlap.

EN 10088-2 X8CrMnCuN17-8-3 (EN 10088-2:2014) and EN 10088-1 X8CrMnCuN17-8-3 (EN 10088-1:2023) are both steel grades. Both fall under the Stainless Steel category. EN 10088-2 X8CrMnCuN17-8-3 is defined under European Standard (EN), originating from Europe, while EN 10088-1 X8CrMnCuN17-8-3 is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10088-2 X8CrMnCuN17-8-3 vs EN 10088-1 X8CrMnCuN17-8-3 is a 100% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 100%.

Frequently Compared With EN 10088-2 X8CrMnCuN17-8-3:
ASTM A959 .- GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4006
Match Breakdown
CHEMISTRY MATCH
100%
MECHANICAL MATCH
No shared data
OVERALL
100%
Specifications
Property EN 10088-2 X8CrMnCuN17-8-3 EN 10088-1 X8CrMnCuN17-8-3
Standard EN 10088-2:2014 EN 10088-1:2023
Category Stainless Steel Stainless Steel
C (%) <=0.10 <=0.10
Si (%) <=2.00 <=2.00
Mn (%) 6.5-9.0 6.5-9.0
P (%) <=0.040 <=0.040
S (%) <=0.030 <=0.030
Cr (%) 15.0-18.0 15.0-18.0
Mo (%) <=1.00 <=1.00
Ni (%) <=3.00 <=3.00
N (%) 0.10-0.30 0.10-0.30
Cu (%) 2.00-3.5 2.00-3.5
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-2 X8CrMnCuN17-8-3 EN 10088-1 X8CrMnCuN17-8-3
Tensile Strength 580-780 MPa Not specified
Yield Strength >=300 MPa Not specified
Elongation >=40% Not specified
Condition Solution annealed (+AT), cold rolled strip, up to 8 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick Not specified
Typical Applications
EN 10088-2 X8CrMnCuN17-8-3
General purposes, hot or cold rolled sheet/plate and strip
EN 10088-1 X8CrMnCuN17-8-3
Not documented
Can EN 10088-2 X8CrMnCuN17-8-3 Be Substituted With EN 10088-1 X8CrMnCuN17-8-3?
EN 10088-2 X8CrMnCuN17-8-3 and EN 10088-1 X8CrMnCuN17-8-3 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X8CrMnCuN17-8-3 is often considered as a substitute for EN 10088-2 X8CrMnCuN17-8-3 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
EN 10088-2 X8CrMnCuN17-8-3
0 active listings and RFQs →
EN 10088-1 X8CrMnCuN17-8-3
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-2 X8CrMnCuN17-8-3 and EN 10088-1 X8CrMnCuN17-8-3?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-2 X8CrMnCuN17-8-3 be substituted with EN 10088-1 X8CrMnCuN17-8-3?
EN 10088-2 X8CrMnCuN17-8-3 and EN 10088-1 X8CrMnCuN17-8-3 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X8CrMnCuN17-8-3 is often considered as a substitute for EN 10088-2 X8CrMnCuN17-8-3 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.