EN 10088-2 X9CrMnNiCu17-8-5-2 vs EN 10088-1 X9CrMnNiCu17-8-5-2

Strong Match — 100% match based on chemical composition and mechanical property overlap.

EN 10088-2 X9CrMnNiCu17-8-5-2 (EN 10088-2:2014) and EN 10088-1 X9CrMnNiCu17-8-5-2 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. EN 10088-2 X9CrMnNiCu17-8-5-2 is defined under European Standard (EN), originating from Europe, while EN 10088-1 X9CrMnNiCu17-8-5-2 is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10088-2 X9CrMnNiCu17-8-5-2 vs EN 10088-1 X9CrMnNiCu17-8-5-2 is a 100% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 100%.

Frequently Compared With EN 10088-2 X9CrMnNiCu17-8-5-2:
IS 1570 (Part 7) 12Cr12MoH EN 10088-1 1.4006 ASTM A959 201 ASTM A959 202 GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 ASTM A959 .- IS 1570 (Part 7) 11Cr17Ni13W3TiH
Match Breakdown
CHEMISTRY MATCH
100%
MECHANICAL MATCH
No shared data
OVERALL
100%
Specifications
Property EN 10088-2 X9CrMnNiCu17-8-5-2 EN 10088-1 X9CrMnNiCu17-8-5-2
Standard EN 10088-2:2014 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.10 <=0.10
Si (%) <=1.00 <=1.00
Mn (%) 5.5-9.5 5.5-9.5
P (%) <=0.070 <=0.070
S (%) <=0.010 <=0.010
Cr (%) 16.5-18.5 16.5-18.5
Ni (%) 4.5-5.5 4.5-5.5
N (%) <=0.15 <=0.15
Cu (%) 1.00-2.50 1.00-2.50
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-2 X9CrMnNiCu17-8-5-2 EN 10088-1 X9CrMnNiCu17-8-5-2
Tensile Strength 540-850 MPa Not specified
Yield Strength >=230 MPa Not specified
Elongation >=45% Not specified
Condition Solution annealed (+AT), cold rolled strip, up to 8 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick Not specified
Typical Applications
EN 10088-2 X9CrMnNiCu17-8-5-2
General purposes, hot or cold rolled sheet/plate and strip
EN 10088-1 X9CrMnNiCu17-8-5-2
Not documented
Can EN 10088-2 X9CrMnNiCu17-8-5-2 Be Substituted With EN 10088-1 X9CrMnNiCu17-8-5-2?
EN 10088-2 X9CrMnNiCu17-8-5-2 and EN 10088-1 X9CrMnNiCu17-8-5-2 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X9CrMnNiCu17-8-5-2 is often considered as a substitute for EN 10088-2 X9CrMnNiCu17-8-5-2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
EN 10088-2 X9CrMnNiCu17-8-5-2
0 active listings and RFQs →
EN 10088-1 X9CrMnNiCu17-8-5-2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-2 X9CrMnNiCu17-8-5-2 and EN 10088-1 X9CrMnNiCu17-8-5-2?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-2 X9CrMnNiCu17-8-5-2 be substituted with EN 10088-1 X9CrMnNiCu17-8-5-2?
EN 10088-2 X9CrMnNiCu17-8-5-2 and EN 10088-1 X9CrMnNiCu17-8-5-2 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X9CrMnNiCu17-8-5-2 is often considered as a substitute for EN 10088-2 X9CrMnNiCu17-8-5-2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.