EN 10088-3 X105CrMo17 vs EN 10088-1 X90CrMoV18

Close Alternative — 70.8% match based on chemical composition and mechanical property overlap.

EN 10088-3 X105CrMo17 (EN 10088-3:2014) and EN 10088-1 X90CrMoV18 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. EN 10088-3 X105CrMo17 is defined under European Standard (EN), originating from Europe, while EN 10088-1 X90CrMoV18 is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10088-3 X105CrMo17 vs EN 10088-1 X90CrMoV18 is a 70.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 70.8%.

Frequently Compared With EN 10088-3 X105CrMo17:
ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
70.8%
MECHANICAL MATCH
No shared data
OVERALL
70.8%
Specifications
Property EN 10088-3 X105CrMo17 EN 10088-1 X90CrMoV18
Standard EN 10088-3:2014 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) 0.95-1.20 0.85-0.95
Si (%) <=1.00 <=1.00
Mn (%) <=1.00 <=1.00
P (%) <=0.040 <=0.040
S (%) <=0.030 <=0.015
Cr (%) 16.0-18.0 17.0-19.0
Mo (%) 0.40-0.80 0.90-1.30
V (%) Not specified 0.07-0.12
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-3 X105CrMo17 EN 10088-1 X90CrMoV18
Hardness <=285 HB Not specified
Condition Annealed (+A), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 100 mm; hardness for guidance only Not specified
Typical Applications
EN 10088-3 X105CrMo17
General purposes, semi-finished products, bars, rods, wire, sections and bright products
EN 10088-1 X90CrMoV18
Not documented
Key Differences
Can EN 10088-3 X105CrMo17 Be Substituted With EN 10088-1 X90CrMoV18?
EN 10088-3 X105CrMo17 and EN 10088-1 X90CrMoV18 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
EN 10088-3 X105CrMo17
0 active listings and RFQs →
EN 10088-1 X90CrMoV18
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-3 X105CrMo17 and EN 10088-1 X90CrMoV18?
EN 10088-1 X90CrMoV18 specifies V which is not specified for EN 10088-3 X105CrMo17.
Can EN 10088-3 X105CrMo17 be substituted with EN 10088-1 X90CrMoV18?
EN 10088-3 X105CrMo17 and EN 10088-1 X90CrMoV18 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.