EN 10088-3 X13MnNiN18-13-2 vs ASTM A276/A276M S24100
Strong Match — 88.9% match
based on chemical composition and mechanical property overlap.
EN 10088-3 X13MnNiN18-13-2 (EN 10088-3:2014) and ASTM A276/A276M S24100 (ASTM A276/A276M:2017) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-3 X13MnNiN18-13-2 is typically used for general purposes, semi-finished products, bars, rods, wire, sections and bright products, while ASTM A276/A276M S24100 is commonly used for stainless steel bars and shapes (hot-finished or cold-finished).
EN 10088-3 X13MnNiN18-13-2 is defined under European Standard (EN), originating from Europe, while ASTM A276/A276M S24100 is defined under ASTM International, originating from United States.
As per chemical composition, EN 10088-3 X13MnNiN18-13-2 vs ASTM A276/A276M S24100 is a 100% match.
As per mechanical properties, the match is 66.7%.
Combined, this makes them a strong match overall at 88.9%.
Frequently Compared With EN 10088-3 X13MnNiN18-13-2:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-3 X13MnNiN18-13-2
ASTM A276/A276M S24100
Tensile Strength
690-850 MPa
>=690 MPa
Yield Strength
>=380 MPa
>=380 MPa
Elongation
>=30%
>=30%
Hardness
<=220 HB
Not specified
Condition
Solution annealed (+AT), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal), hardness for guidance only
Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed)
Typical Applications
EN 10088-3 X13MnNiN18-13-2
General purposes, semi-finished products, bars, rods, wire, sections and bright products
ASTM A276/A276M S24100
Stainless steel bars and shapes (hot-finished or cold-finished)
Can EN 10088-3 X13MnNiN18-13-2 Be Substituted With ASTM A276/A276M S24100?
EN 10088-3 X13MnNiN18-13-2 and ASTM A276/A276M S24100 overlap closely enough on chemistry and mechanical properties that ASTM A276/A276M S24100 is often considered as a substitute for EN 10088-3 X13MnNiN18-13-2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between EN 10088-3 X13MnNiN18-13-2 and ASTM A276/A276M S24100?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-3 X13MnNiN18-13-2 be substituted with ASTM A276/A276M S24100?
EN 10088-3 X13MnNiN18-13-2 and ASTM A276/A276M S24100 overlap closely enough on chemistry and mechanical properties that ASTM A276/A276M S24100 is often considered as a substitute for EN 10088-3 X13MnNiN18-13-2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.