EN 10088-3 X1CrNiMoCuN20-18-7 vs IS 6603 X01Cr20Ni18Mo6CuN
Strong Match — 99.1% match
based on chemical composition and mechanical property overlap.
EN 10088-3 X1CrNiMoCuN20-18-7 (EN 10088-3:2014) and IS 6603 X01Cr20Ni18Mo6CuN (IS 6603:2024) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-3 X1CrNiMoCuN20-18-7 is typically used for general purposes, semi-finished products, bars, rods, wire, sections and bright products, while IS 6603 X01Cr20Ni18Mo6CuN is commonly used for general purposes, semi-finished products, bars, wire rods and bright bars.
EN 10088-3 X1CrNiMoCuN20-18-7 is defined under European Standard (EN), originating from Europe, while IS 6603 X01Cr20Ni18Mo6CuN is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, EN 10088-3 X1CrNiMoCuN20-18-7 vs IS 6603 X01Cr20Ni18Mo6CuN is a 98.7% match.
As per mechanical properties, the match is 100%.
Combined, this makes them a strong match overall at 99.1%.
Frequently Compared With EN 10088-3 X1CrNiMoCuN20-18-7:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-3 X1CrNiMoCuN20-18-7
IS 6603 X01Cr20Ni18Mo6CuN
Tensile Strength
650-850 MPa
650-850 MPa
Yield Strength
>=300 MPa
>=300 MPa
Elongation
>=35%
>=35%
Hardness
<=260 HB
Not specified
Condition
Solution annealed (+AT), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal), hardness for guidance only
Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal)
Typical Applications
EN 10088-3 X1CrNiMoCuN20-18-7
General purposes, semi-finished products, bars, rods, wire, sections and bright products
IS 6603 X01Cr20Ni18Mo6CuN
General purposes, semi-finished products, bars, wire rods and bright bars
Can EN 10088-3 X1CrNiMoCuN20-18-7 Be Substituted With IS 6603 X01Cr20Ni18Mo6CuN?
EN 10088-3 X1CrNiMoCuN20-18-7 and IS 6603 X01Cr20Ni18Mo6CuN overlap closely enough on chemistry and mechanical properties that IS 6603 X01Cr20Ni18Mo6CuN is often considered as a substitute for EN 10088-3 X1CrNiMoCuN20-18-7 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between EN 10088-3 X1CrNiMoCuN20-18-7 and IS 6603 X01Cr20Ni18Mo6CuN?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-3 X1CrNiMoCuN20-18-7 be substituted with IS 6603 X01Cr20Ni18Mo6CuN?
EN 10088-3 X1CrNiMoCuN20-18-7 and IS 6603 X01Cr20Ni18Mo6CuN overlap closely enough on chemistry and mechanical properties that IS 6603 X01Cr20Ni18Mo6CuN is often considered as a substitute for EN 10088-3 X1CrNiMoCuN20-18-7 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.