Close Alternative — 71.7% match
based on chemical composition and mechanical property overlap.
EN 10088-3 X1CrNiMoCuN25-25-5 (EN 10088-3:2014) and ASTM A959 904L (ASTM A959:2011) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-3 X1CrNiMoCuN25-25-5 is typically used for general purposes, semi-finished products, bars, rods, wire, sections and bright products, while ASTM A959 904L is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1).
EN 10088-3 X1CrNiMoCuN25-25-5 is defined under European Standard (EN), originating from Europe, while ASTM A959 904L is defined under ASTM International, originating from United States.
As per chemical composition, EN 10088-3 X1CrNiMoCuN25-25-5 vs ASTM A959 904L is a 71.7% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a close alternative overall at 71.7%.
Frequently Compared With EN 10088-3 X1CrNiMoCuN25-25-5:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-3 X1CrNiMoCuN25-25-5
ASTM A959 904L
Tensile Strength
600-800 MPa
Not specified
Yield Strength
>=300 MPa
Not specified
Elongation
>=35%
Not specified
Hardness
<=250 HB
Not specified
Condition
Solution annealed (+AT), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal), hardness for guidance only
Not specified
Typical Applications
EN 10088-3 X1CrNiMoCuN25-25-5
General purposes, semi-finished products, bars, rods, wire, sections and bright products
ASTM A959 904L
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Can EN 10088-3 X1CrNiMoCuN25-25-5 Be Substituted With ASTM A959 904L?
EN 10088-3 X1CrNiMoCuN25-25-5 and ASTM A959 904L are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
What is the difference between EN 10088-3 X1CrNiMoCuN25-25-5 and ASTM A959 904L?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-3 X1CrNiMoCuN25-25-5 be substituted with ASTM A959 904L?
EN 10088-3 X1CrNiMoCuN25-25-5 and ASTM A959 904L are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.