EN 10088-3 X1CrNiMoCuN25-25-5 vs EN 10088-1 X1CrNi25-21

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

EN 10088-3 X1CrNiMoCuN25-25-5 (EN 10088-3:2014) and EN 10088-1 X1CrNi25-21 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. EN 10088-3 X1CrNiMoCuN25-25-5 is defined under European Standard (EN), originating from Europe, while EN 10088-1 X1CrNi25-21 is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10088-3 X1CrNiMoCuN25-25-5 vs EN 10088-1 X1CrNi25-21 is a 71% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With EN 10088-3 X1CrNiMoCuN25-25-5:
EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
71%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property EN 10088-3 X1CrNiMoCuN25-25-5 EN 10088-1 X1CrNi25-21
Standard EN 10088-3:2014 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.020 <=0.020
Si (%) <=0.70 <=0.25
Mn (%) <=2.00 <=2.00
P (%) <=0.030 <=0.025
S (%) <=0.010 <=0.010
Cr (%) 24.0-26.0 24.0-26.0
Mo (%) 4.7-5.7 <=0.20
Ni (%) 24.0-27.0 20.0-22.0
N (%) 0.17-0.25 <=0.10
Cu (%) 1.00-2.00 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-3 X1CrNiMoCuN25-25-5 EN 10088-1 X1CrNi25-21
Tensile Strength 600-800 MPa Not specified
Yield Strength >=300 MPa Not specified
Elongation >=35% Not specified
Hardness <=250 HB Not specified
Condition Solution annealed (+AT), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal), hardness for guidance only Not specified
Typical Applications
EN 10088-3 X1CrNiMoCuN25-25-5
General purposes, semi-finished products, bars, rods, wire, sections and bright products
EN 10088-1 X1CrNi25-21
Not documented
Key Differences
Can EN 10088-3 X1CrNiMoCuN25-25-5 Be Substituted With EN 10088-1 X1CrNi25-21?
EN 10088-3 X1CrNiMoCuN25-25-5 and EN 10088-1 X1CrNi25-21 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
EN 10088-3 X1CrNiMoCuN25-25-5
0 active listings and RFQs →
EN 10088-1 X1CrNi25-21
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-3 X1CrNiMoCuN25-25-5 and EN 10088-1 X1CrNi25-21?
EN 10088-3 X1CrNiMoCuN25-25-5 specifies Cu which is not specified for EN 10088-1 X1CrNi25-21.
Can EN 10088-3 X1CrNiMoCuN25-25-5 be substituted with EN 10088-1 X1CrNi25-21?
EN 10088-3 X1CrNiMoCuN25-25-5 and EN 10088-1 X1CrNi25-21 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.