EN 10088-3 X1NiCrMoCu25-20-5 vs GOST 5632 08X18H10
Minimal Match — 33.1% match
based on chemical composition and mechanical property overlap.
EN 10088-3 X1NiCrMoCu25-20-5 (EN 10088-3:2014) and GOST 5632 08X18H10 (GOST 5632-2014) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-3 X1NiCrMoCu25-20-5 is typically used for general purposes, semi-finished products, bars, rods, wire, sections and bright products, while GOST 5632 08X18H10 is commonly used for chemical equipment, food processing, general corrosion resistant applications.
EN 10088-3 X1NiCrMoCu25-20-5 is defined under European Standard (EN) (Europe).
As per chemical composition, EN 10088-3 X1NiCrMoCu25-20-5 vs GOST 5632 08X18H10 is a 49.6% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 33.1%.
Frequently Compared With EN 10088-3 X1NiCrMoCu25-20-5:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-3 X1NiCrMoCu25-20-5
GOST 5632 08X18H10
Tensile Strength
530-730 MPa
≥520 MPa
Yield Strength
>=230 MPa
≥205 MPa
Elongation
>=35%
≥40%
Hardness
<=230 HB
Not specified
Condition
Solution annealed (+AT), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal), hardness for guidance only
Not specified
Typical Applications
EN 10088-3 X1NiCrMoCu25-20-5
General purposes, semi-finished products, bars, rods, wire, sections and bright products
GOST 5632 08X18H10
Chemical equipment, food processing, general corrosion resistant applications
Key Differences
EN 10088-3 X1NiCrMoCu25-20-5 specifies Mo, N, Cu which are not specified for GOST 5632 08X18H10.
Can EN 10088-3 X1NiCrMoCu25-20-5 Be Substituted With GOST 5632 08X18H10?
EN 10088-3 X1NiCrMoCu25-20-5 and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between EN 10088-3 X1NiCrMoCu25-20-5 and GOST 5632 08X18H10?
EN 10088-3 X1NiCrMoCu25-20-5 specifies Mo, N, Cu which are not specified for GOST 5632 08X18H10.
Can EN 10088-3 X1NiCrMoCu25-20-5 be substituted with GOST 5632 08X18H10?
EN 10088-3 X1NiCrMoCu25-20-5 and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.