EN 10088-3 X1NiCrMoCu31-27-4 vs GB/T 3280 06Cr19Ni10

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

EN 10088-3 X1NiCrMoCu31-27-4 (EN 10088-3:2014) and GB/T 3280 06Cr19Ni10 (GB/T 3280-2015) are both steel grades. Both fall under the Stainless Steel category. EN 10088-3 X1NiCrMoCu31-27-4 is typically used for general purposes, semi-finished products, bars, rods, wire, sections and bright products, while GB/T 3280 06Cr19Ni10 is commonly used for used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners.. EN 10088-3 X1NiCrMoCu31-27-4 is defined under European Standard (EN), originating from Europe, while GB/T 3280 06Cr19Ni10 is defined under Guobiao Standards (GB/T), originating from China.

As per chemical composition, EN 10088-3 X1NiCrMoCu31-27-4 vs GB/T 3280 06Cr19Ni10 is a 58.8% match. As per mechanical properties, the match is 20%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With EN 10088-3 X1NiCrMoCu31-27-4:
ASTM A959 26-3-3 ASTM A959 .- GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
58.8%
MECHANICAL MATCH
20%
OVERALL
35%
Specifications
Property EN 10088-3 X1NiCrMoCu31-27-4 GB/T 3280 06Cr19Ni10
Standard EN 10088-3:2014 GB/T 3280-2015
Category Stainless Steel Stainless Steel
C (%) <=0.020 0.08 max
Si (%) <=0.70 1.00 max
Mn (%) <=2.00 2.00 max
P (%) <=0.030 0.045 max
S (%) <=0.010 0.030 max
Cr (%) 26.0-28.0 18.00-20.00
Mo (%) 3.0-4.0 Not specified
Ni (%) 30.0-32.0 8.00-11.00
N (%) <=0.10 Not specified
Cu (%) 0.70-1.50 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-3 X1NiCrMoCu31-27-4 GB/T 3280 06Cr19Ni10
Tensile Strength 500-750 MPa 520-720 MPa
Yield Strength >=220 MPa 205-310 MPa
Elongation >=35% 40-60%
Hardness <=230 HB 187 HB max
Condition Solution annealed (+AT), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal), hardness for guidance only Not specified
Typical Applications
EN 10088-3 X1NiCrMoCu31-27-4
General purposes, semi-finished products, bars, rods, wire, sections and bright products
GB/T 3280 06Cr19Ni10
Used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners.
Key Differences
Can EN 10088-3 X1NiCrMoCu31-27-4 Be Substituted With GB/T 3280 06Cr19Ni10?
EN 10088-3 X1NiCrMoCu31-27-4 and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
EN 10088-3 X1NiCrMoCu31-27-4
No active listings currently.
GB/T 3280 06Cr19Ni10
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2900–3300 mm (114.17–129.92 in)
On M-EX Right Now
EN 10088-3 X1NiCrMoCu31-27-4
0 active listings and RFQs →
GB/T 3280 06Cr19Ni10
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-3 X1NiCrMoCu31-27-4 and GB/T 3280 06Cr19Ni10?
EN 10088-3 X1NiCrMoCu31-27-4 specifies Mo, N, Cu which are not specified for GB/T 3280 06Cr19Ni10.
Can EN 10088-3 X1NiCrMoCu31-27-4 be substituted with GB/T 3280 06Cr19Ni10?
EN 10088-3 X1NiCrMoCu31-27-4 and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.