Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
EN 10088-3 X20Cr13 (EN 10088-3:2014) and GOST 5632 08X18H10 (GOST 5632-2014) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-3 X20Cr13 is typically used for general purposes, semi-finished products, bars, rods, wire, sections and bright products, while GOST 5632 08X18H10 is commonly used for chemical equipment, food processing, general corrosion resistant applications.
EN 10088-3 X20Cr13 is defined under European Standard (EN) (Europe).
As per chemical composition, EN 10088-3 X20Cr13 vs GOST 5632 08X18H10 is a 62.7% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 35%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-3 X20Cr13
GOST 5632 08X18H10
Tensile Strength
<=760 MPa
≥520 MPa
Hardness
<=230 HB
Not specified
Condition
Annealed (+A), conditions 1C, 1E, 1D, 1X, 1G and 2D, size range not stated; hardness for guidance only
Not specified
Yield Strength
Not specified
≥205 MPa
Elongation
Not specified
≥40%
Typical Applications
EN 10088-3 X20Cr13
General purposes, semi-finished products, bars, rods, wire, sections and bright products
GOST 5632 08X18H10
Chemical equipment, food processing, general corrosion resistant applications
Key Differences
GOST 5632 08X18H10 specifies Ni which is not specified for EN 10088-3 X20Cr13.
Can EN 10088-3 X20Cr13 Be Substituted With GOST 5632 08X18H10?
EN 10088-3 X20Cr13 and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between EN 10088-3 X20Cr13 and GOST 5632 08X18H10?
GOST 5632 08X18H10 specifies Ni which is not specified for EN 10088-3 X20Cr13.
Can EN 10088-3 X20Cr13 be substituted with GOST 5632 08X18H10?
EN 10088-3 X20Cr13 and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.