EN 10088-3 X29CrS13 vs EN 10088-1 1.4006

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

EN 10088-3 X29CrS13 (EN 10088-3:2014) and EN 10088-1 1.4006 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. EN 10088-3 X29CrS13 is typically used for general purposes, semi-finished products, bars, rods, wire, sections and bright products, while EN 10088-1 1.4006 is commonly used for cutlery, turbine blades, fasteners, surgical instruments. EN 10088-3 X29CrS13 is defined under European Standard (EN), originating from Europe, while EN 10088-1 1.4006 is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10088-3 X29CrS13 vs EN 10088-1 1.4006 is a 68% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With EN 10088-3 X29CrS13:
GOST 5632 06Kh23N28 EN 10088-1 1.4845 ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr13H IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
68%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property EN 10088-3 X29CrS13 EN 10088-1 1.4006
Standard EN 10088-3:2014 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) 0.25-0.32 0.08–0.15
Si (%) <=1.00 ≤1.00
Mn (%) <=1.50 ≤1.50
P (%) <=0.040 Not specified
S (%) 0.15-0.25 Not specified
Cr (%) 12.0-13.5 11.5–13.5
Mo (%) <=0.60 Not specified
Ni (%) Not specified ≤0.75
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-3 X29CrS13 EN 10088-1 1.4006
Tensile Strength <=800 MPa ≥540 MPa (annealed)
Hardness <=245 HB Not specified
Condition Annealed (+A), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; hardness for guidance only Not specified
Hardness HRC Not specified 36–45 (hardened)
Elongation Not specified ≥18%
Typical Applications
EN 10088-3 X29CrS13
General purposes, semi-finished products, bars, rods, wire, sections and bright products
EN 10088-1 1.4006
Cutlery, turbine blades, fasteners, surgical instruments
Key Differences
Can EN 10088-3 X29CrS13 Be Substituted With EN 10088-1 1.4006?
EN 10088-3 X29CrS13 and EN 10088-1 1.4006 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
EN 10088-3 X29CrS13
No active listings currently.
EN 10088-1 1.4006
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2700–3400 mm (106.3–133.86 in)
On M-EX Right Now
EN 10088-3 X29CrS13
0 active listings and RFQs →
EN 10088-1 1.4006
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-3 X29CrS13 and EN 10088-1 1.4006?
EN 10088-3 X29CrS13 specifies P, S, Mo which are not specified for EN 10088-1 1.4006. EN 10088-1 1.4006 specifies Ni which is not specified for EN 10088-3 X29CrS13.
Can EN 10088-3 X29CrS13 be substituted with EN 10088-1 1.4006?
EN 10088-3 X29CrS13 and EN 10088-1 1.4006 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.